Macromolecular deodorizer and preparation process thereof

A deodorant and polymer technology, applied in the field of polymer deodorant and its preparation process, can solve the problems of incompatibility and discount of deodorant effect, and achieve the effect of simple processing and low cost

Active Publication Date: 2013-01-02
王建华
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the important deodorizing method in the currently used polymer deodorants is only the use of organic polymer flocculants. Although the effect is good, it cannot combine with all odor molecules, which greatly reduces the deodorization effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecular deodorizer and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A polymer deodorant, the preparation process is as follows:

[0032] 1. Take 10 parts of inorganic polymer coagulant and add it to 100 parts of water. Stir continuously during the addition process so that no fish-eye flocs are produced. In order to dissolve thoroughly, the water can be properly warmed. Prepare an inorganic polymer coagulant solution.

[0033] 2. Take 7 parts of natural polymer coagulant and add it to 100 parts of water. Stir continuously during the addition process so that no fish-eye flocs are produced. In order to dissolve thoroughly, the water can be properly warmed. Made of natural polymer coagulant solution.

[0034] 3. Dissolve 3 parts of defoaming agent in 50 parts of water, take 5 parts of its aqueous solution and add it into the natural polymer coagulant solution. Be careful to stir constantly while adding.

[0035] 4. Mix the above two polymer coagulant solutions. Note that when mixing, slowly add the prepared inorganic polymer coagula...

Embodiment 2

[0086] A polymer deodorant, comprising the following raw materials in parts by weight:

[0087] Inorganic polymer coagulant 5 Natural polymer coagulant 10

[0088] Defoamer 1 Antimicrobial 1.5

[0089] Bactericide 0.5.

[0090] The production process is the same as the preparation process of Example 1.

Embodiment 3

[0092] A polymer deodorant, comprising the following raw materials in parts by weight:

[0093] Inorganic polymer coagulant 15 Natural polymer coagulant 5

[0094] Defoamer 5 Antibacterial agent 0.5

[0095] Bactericide 1.5.

[0096] The production process is the same as the preparation process of Example 1.

[0097] Features of dual-media polymer deodorant

[0098] 1. Instantly eliminate odor

[0099] When the odor molecules meet the huge microgel, the strong attraction will firmly attach the odor molecules to the polymer network. Odor molecules can be divided into acidic or alkaline, neutral odor, but regardless of the nature of the odor molecule, the dual-media polymer deodorant can achieve the same effect as activated carbon adsorption to achieve the instant odor elimination effect.

[0100] 2. Positive and negative ion efficiency

[0101] The biggest weapon of ultragel is that the polymer structure has the function of positive and negative zwitterions. Many deodora...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a macromolecular deodorizer comprising the following raw materials in parts by weight: 5 to 15 parts of inorganic macromolecular coagulant, 5 to 10 parts of natural macromolecular coagulant, 1 to 5 parts of defoaming agent, 0.5 to 1.5 parts of antimicrobial and 0.5 to 1.5 parts of degerming agent. The invention also discloses a preparation process of the macromolecular deodorizer. The invention realizes instant absorption for all odor molecules by taking full use of the flocculation capability of inorganic macromolecules and natural macromolecules, enables a deodorization effect to be largely excellent to the deodorization effects of various deodorizers, has simple processing and low cost and meets the large-quantity utilization in the consumption markets of deodorization liquid in China.

Description

technical field [0001] The invention relates to a deodorant, in particular to a polymer deodorant and a preparation process thereof. Background technique [0002] With the continuous in-depth development of my country's economic construction, garbage, domestic waste water, and the odor produced by industrial production are also constantly increasing. It not only affects the senses of the residents, but also has a great impact on the health of the residents. [0003] At present, the deodorants commonly used at home and abroad mainly include: natural plant liquid deodorants, biological deodorants, aromatic deodorants, polymer deodorants, charcoal exudate deodorants and other major categories of products. Among them, natural plant liquid deodorants, aroma deodorants, and charcoal exudate deodorants are covered deodorants. Specifically, they do not eliminate odors, but add fragrances to odors to neutralize them. Make it sensory to reduce the impact of odor. Biological deodora...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L9/012A61L9/013A61L9/014A61L101/56A61L101/50A61L101/28A61L101/24
Inventor 王建华
Owner 王建华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com