Method for manufacturing electric steel with excellent longitudinal magnetic performance

A manufacturing method and technology of magnetic properties, applied in the field of electrical steel manufacturing, can solve problems such as difficulty in controlling the nucleation of oriented grains

Active Publication Date: 2010-03-03
ANGANG STEEL CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a method for manufacturing electrical steel products with excellent longitudinal magnetic properties, which solves the problem that the nucleation and growth of each orientation grain are difficult ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing electric steel with excellent longitudinal magnetic performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A kind of manufacturing method of electrical steel with excellent longitudinal magnetic performance of the present invention, the technological route adopted is: smelting, continuous casting, hot rolling, hot-rolled sheet normalization, cold rolling and annealing, it is characterized in that the hot-rolled sheet normalization treatment is in It is carried out in the same external magnetic field as the rolling direction, the normalization treatment temperature is lower than the Curie temperature of the steel, and the heating temperature is 700-760°C. The external magnetic field can be a DC magnetic field, an AC magnetic field or a pulsed magnetic field. Normalization treatment is isothermal treatment below the Curie temperature.

[0011] The non-extractable electrical steel with different silicon content is smelted by converter, RH refining treatment, and continuous casting into 250mm thick continuous casting slab. The slab is heated and rolled to 2.5mm thick. Without h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing electric steel with excellent longitudinal magnetic performance, which adopts a process route of smelting, continuous casting, hot rolling, normalizing of a hot-rolled sheet, cold rolling and annealing, and is characterized in that: the temperature in the normalizing of the hot-rolled sheet is lower than Curie temperature of the steel, the heatingtemperature is between 700 and 760DEG C, and the normalizing is performed in a magnetic field with an applied field strength between 3,000 and 9,000e in the rolling direction. Under the action of themagnetic field, complex magnetic domains generated by the influence of lattice deformation, precipitation and micro-area defects in a material are oriented in micro magnetic areas in the outer magnetic field direction, partial micro-area structures are restored and changed because of the action of thermokinetics, magnetic domains vertical to the outer magnetic field direction are decreased, and magnetic domains parallel to the outer magnetic filed direction are increased, so the uniaxial anisotropy along the outer magnetic field direction is induced and the longitudinal magnetic performance of products is improved.

Description

technical field [0001] The invention relates to a manufacturing method of electrical steel strip (plate), in particular to a manufacturing method of electrical steel for obtaining excellent longitudinal magnetic properties. Background technique [0002] Electrical steel is an important metal functional material, which is used to prepare the iron core of the electromagnetic conversion carrier and is used in various fields of the national economy. In its application process, the iron core often needs directional magnetic conduction to play the important functions of voltage conversion, frequency conversion, and signal processing. For example, non-oriented electrical steel is often used to make micro-miniature transformers, voltage stabilizers, current stabilizers and signal processing chips through longitudinal cutting; while grain-oriented electrical steel is more widely used because of its unique longitudinal orientation characteristics, and is often used to manufacture larg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D8/12
Inventor 高振宇张智义金文旭李文权张仁波冷显国李亚东罗理刘立新
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap