Hydroxyapatite toothpaste

A hydroxyapatite and toothpaste technology, used in dentistry, medical science, oral care, etc., can solve the problems of inapplicable oral ulcer patients and aggravation of oral ulcer patients, so as to relieve gingival swelling and pain, protect teeth, inhibit oral cavity effect of bacteria

Active Publication Date: 2016-02-17
SANJIAO ORAL HEALTH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current toothpastes on the market are not suitable for patients with oral ulcers, and may even aggravate the condition of some patients with oral ulcers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A hydroxyapatite-type toothpaste, consisting of the following components by weight percentage: 35% hydroxyapatite, 35% 1,2-propanediol, 3% sodium lauroyl amphoteric PG-acetate phosphate, 2 % sodium alginate, 2% stevia, 2% Chinese herbal medicine extract, and the balance is water.

[0026] The Chinese medicinal material extract is composed of the following components in parts by weight: 20 parts of honeysuckle water extract, 20 parts of white peony water extract, 10 parts of Poria cocos alcohol extract, and 10 parts of schisandra alcohol extract. The Chinese medicinal material extract is obtained by simply mixing the honeysuckle water extract, the white peony water extract, the poria cocos alcohol extract and the schisandra alcohol extract.

[0027] The hydroxyapatite toothpaste of the present invention can be prepared by conventional methods in the art. Specifically, the preparation method of the hydroxyapatite-type toothpaste in this embodiment is as follows: after we...

Embodiment 2

[0029] A hydroxyapatite-type toothpaste, consisting of the following components by weight percentage: 35% hydroxyapatite, 35% 1,2-propanediol, 3% sodium lauroyl amphoteric PG-acetate phosphate, 2 % sodium alginate, 2% stevia, 2% Chinese herbal medicine extract, and the balance is water.

[0030] The Chinese medicinal material extract is composed of the following components in parts by weight: 20 parts of white peony water extract, 10 parts of poria cocos alcohol extract, and 10 parts of schisandra alcohol extract.

[0031] According to the preparation method of Example 1, the hydroxyapatite toothpaste of Example 2 was obtained.

Embodiment 3

[0033] A hydroxyapatite-type toothpaste, consisting of the following components by weight percentage: 35% hydroxyapatite, 35% 1,2-propanediol, 3% sodium lauroyl amphoteric PG-acetate phosphate, 2 % sodium alginate, 2% stevia, 2% Chinese herbal medicine extract, and the balance is water.

[0034] The Chinese medicinal material extract is composed of the following components in parts by weight: 20 parts of honeysuckle water extract, 10 parts of Poria cocos alcohol extract, and 10 parts of schisandra alcohol extract.

[0035] According to the preparation method of Example 1, the hydroxyapatite toothpaste of Example 3 was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to hydroxyapatite type toothpaste. The hydroxyapatite type toothpaste comprises, by weight, 30-40% of hydroxyapatite, 20-40% of 1,2-propylene glycol, 2.5-3.5% of sodium lauroampho PG-acetate phosphate, 1-3% of sodium alginate, 1-3% of stevioside, and the balance water. The hydroxyapatite type toothpaste can effectively inhibit oral bacteria, protect teeth and refresh breath, and also is applicable to patients suffering from oral ulcers to relieve symptoms such as swelling and aching of gums.

Description

technical field [0001] The invention relates to a toothpaste, in particular to a hydroxyapatite toothpaste. Background technique [0002] Toothpaste is a daily necessities that is used with toothbrush to clean teeth, protect oral hygiene, and is safe for human body. With the improvement of people's living standards, the quality demand for toothpaste is also gradually increasing. In terms of performance, toothpaste is generally required to: (1) be able to remove the film and plaque on the tooth surface without damaging the enamel and dentin; (2) have a good effect on cleaning the oral cavity and its surroundings; No irritation to the mucous membrane; (4) It has a comfortable fragrance and taste, and has a cool and fresh feeling after use. [0003] However, the current toothpastes on the market are not suitable for patients with oral ulcers, and may even aggravate the condition of some patients with oral ulcers. Contents of the invention [0004] Aiming at the above-menti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/73A61K8/99A61K8/97A61K8/24A61Q11/00
Inventor 宋繁华
Owner SANJIAO ORAL HEALTH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com