Double-layer cemented carbide substrate and preparation method thereof

A cemented carbide substrate and cemented carbide technology are applied in the field of double-layer cemented carbide substrate and its preparation, which can solve the problems of high production cost, unstable product performance, poor repeatability, reliability and consistency, etc. Simple and controllable manufacturing, high repeatability of product performance

Active Publication Date: 2016-02-17
潜江新锐硬质合金工具有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above methods have high production costs, complex processes, and are difficult to control. They are likely to cause unstable product performance, poor repeatability, reliability, and consistency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-layer cemented carbide substrate and preparation method thereof
  • Double-layer cemented carbide substrate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] Such as figure 1 As shown, the double-layer cemented carbide substrate includes a first cemented carbide body 1 with a U-shaped structure and a second cemented carbide body 2 covered by the first cemented carbide body. The first cemented carbide body 1 is a medium-high cobalt cemented carbide, and the second cemented carbide body 2 is a medium-low cobalt cemented carbide. The second cemented carbide body 2 is convexly provided with a protruding part 3, and the shape of the protruding part 3 is a frustum of a cone, a sphere or Spherical shape, the centerline of the first cemented carbide body 1 is coaxial with the centerline of the second cemented carbide body 2, the cobalt content in the first cemented carbide body 1 is 10% to 25%, the second cemented carbide body The cobalt content in body 2 is 5% to 15%.

[0020] The preparation process of the double-layer cemented carbide substrate: first, preform a cylindrical second cemented carbide body 2 with a protrusion 3, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a double-layer hard alloy matrix and production method thereof. The double-layer hard alloy matrix comprises a U-shaped structured first hard alloy body and a second hard alloy body; the first hard alloy body covers the second hard alloy body; the first hard alloy body is medium-high cobalt hard alloy; the second hard alloy body is medium-low cobalt hard alloy. The production method of the double-layer hard alloy matrix comprises preforming the second hard alloy body; positioning through a protruding portion of the second hard alloy body; forming into the second hard alloy body; forming into a U-shaped structured double-layer hard alloy base plate by sintering through a lower temperature sintering furnace. According to the double-layer hard alloy matrix and the production method thereof, two hard alloy of the U-shaped structured double-layer hard alloy matrix has clear boundary surfaces and different metallographical structures, the production is simple and controllable, and repeatability of the product performance is high.

Description

technical field [0001] The invention relates to a double-layer cemented carbide substrate and a preparation method thereof, belonging to the technical field of cemented carbide powder metallurgy. Background technique [0002] In the cemented carbide matrix products for PDC, the cemented carbide used in the matrix is ​​usually a cemented carbide with a single cobalt content of 8% to 20%. Cemented carbide supports the diamond layer with higher wear resistance in PDC products, and can absorb the impact caused by PDC during use. When cemented carbide with single cobalt content is compounded with diamond micropowder under high temperature and high pressure to form PDC, the cobalt in the cemented carbide will migrate to the diamond layer, resulting in the loss of cobalt in the cemented carbide and reducing the support of the matrix. The supporting effect of the cemented carbide matrix with low cobalt content is lower than that of the matrix with high cobalt content, and the matri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F7/06B22F3/16
Inventor 李雄明余立新陆庆忠
Owner 潜江新锐硬质合金工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com