Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of automobile filter filter paper coating material and preparation method thereof

A technology of coating materials and filters, applied in papermaking, pigmented coatings, textiles and papermaking, etc., to achieve the effects of high air permeability, simple process and obvious comprehensive effect

Active Publication Date: 2016-08-17
北京联飞翔科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problems existing in the existing filter paper, the present invention aims to provide a new type of filter paper coating material for automotive environmental protection filters and its preparation by using the composite technology of high aspect ratio natural mineral material nanofibers and in-use automotive filter paper papermaking fibers method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of automobile filter filter paper coating material and preparation method thereof
  • A kind of automobile filter filter paper coating material and preparation method thereof
  • A kind of automobile filter filter paper coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Preparation of far-infrared ceramic powder:

[0038] 0.9kg of magnesium tourmaline ultrafine powder with a median diameter of 0.5μm, and La with a median diameter of 0.21μm 2 o 3 0.1kg, Fe 2 o 3 0.2kg, MnO 2 0.3kg, Co 2 o 3 0.1kg, CuO 0.2kg.

[0039] 2. Preparation of filter paper coating material:

[0040] 1) Add the silane coupling agent and diluent to the far-infrared ceramic powder and stir for 20 minutes, let it stand for 8 minutes, and dry at 100°C; improve the surface properties of the ceramic powder, make it better integrated with the pulp, and increase the powder in the paper of firmness.

[0041] 2) Add the far-infrared ceramic powder, sepiolite nanofiber, synthetic fiber, sizing agent and styrene-acrylic emulsion after the surface pretreatment in step 1) into the beaten wood pulp at the same time, and use mechanical stirring to make it evenly mixed. Then add water to adjust the concentration to 3.2%, and the obtained slurry is the coating mate...

Embodiment 2

[0052] 1. Preparation of far-infrared ceramic powder:

[0053] 1.9kg of ferrite ultrafine powder with a median diameter of 1.4μm, and CeO with a median diameter of 0.08μm 2 0.2kg, Fe 2 o 3 0.3kg, MnO 2 0.3kg, Co 2 o 3 0.8kg, CuO 0.2kg.

[0054] 2. Preparation of filter paper coating material:

[0055] The coating material was prepared according to the method of Example 1. Among them, high-aspect-ratio sepiolite nanofibers were prepared by high-speed airflow technology, with a diameter of 81 nm and a length of 0.11 μm.

[0056] Cut the synthetic fiber with a cutting machine, the length is less than 2cm.

[0057] Among them, the distribution ratio of each group is shown in Table 3.

[0058] The proportioning (kg) of table 3 embodiment 2

[0059]

[0060] Use the prepared coating material with a mass area ratio of 50g / m 2 Coated on the filter paper of the diesel filter, dried to make the filter paper of the environment-friendly diesel filter. The results of pape...

Embodiment 3

[0065] 1. Preparation of far-infrared ceramic powder:

[0066] 3.1kg of lithium tourmaline ultrafine powder with a median diameter of 1.1μm, and Ce with a median diameter of 1.7μm 2 o 3 0.2kg, Fe 2 o 3 0.8kg, MnO 2 0.3kg, Co 2 o 3 0.2kg, CuO 1.2kg.

[0067] 2. Preparation of filter paper coating material:

[0068] The coating material was prepared according to the method of Example 1. Among them, high-aspect-ratio sepiolite nanofibers were prepared by high-speed airflow technology, with a diameter of 92 nm and a length of 0.22 μm.

[0069] The synthetic fiber is cut with a cutting machine, and the length is less than 1.5cm.

[0070] Among them, the distribution ratio of each group is shown in Table 5.

[0071] The proportioning (kg) of table 5 embodiment 3

[0072]

[0073] Use the prepared coating material with a mass area ratio of 50g / m 2 Coated on the filter paper of gasoline filter, and dried to make the filter paper of environment-friendly gasoline filte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a filter paper coating material for auto filters, and the filter paper coating material for auto filters is prepared from the following components in parts by weight: 1-6 parts of far infrared ceramic powder, 2-20 parts of sepiolite nano fiber, 4-10 parts of synthetic fiber, 0.8-2 parts of silane coupling agent, 0.8-2 parts of diluent, 9-20 parts of sizing agent, 20-40 parts of styrene-acrylic emulsion and 60-96 parts of wood pulp. According to the coating material provided by the invention, the manufactured air, fuel and oil filters have remarkable comprehensive functions, the motor vehicle exhaust emission is decreased by 13-40%, the dynamic performance is improved by 5-15%, the fuel can be saved by 2-7% and the emission standard is up to the European standard IV.

Description

technical field [0001] The invention relates to a filter paper coating material for an automobile filter, in particular to a filter material coating material with an environmental protection function and a manufacturing method thereof, belonging to the technical field of automobile environmental protection. Background technique [0002] The rapid development of the automobile industry has brought prosperity and convenience to mankind. However, with the sharp increase in the number of automobiles, the environmental problems caused by automobile emissions have emerged. Nitrogen oxides, volatile organic compounds and inhalable particulate matter in emissions have contributed 66%, 90% and 26% of all pollution sources in urban central areas, respectively. Automobile filters have the function of filtering fuel, air and engine oil. The filter element is its main filtering part and undertakes the filtering work. The research on filter materials is directly related to the filtering e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H19/40D21H19/36D21H21/16D21H21/14
Inventor 郑淑芬金伟
Owner 北京联飞翔科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com