Diisopropyl phenylphosphinate flame retardant composition and application method thereof

A technology of diisopropyl phenylphosphinate and its application method, which is applied in the field of diisopropyl phenylphosphinate flame retardant compositions, can solve the problems of high application cost, flame retardancy and plasticizing properties of chlorinated paraffin Not very good, expensive and other problems, to achieve the effect of convenient application, lower application cost, and improved compatibility

Active Publication Date: 2017-01-11
RES INST OF XIANGCHENG SUZHOU UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because chlorinated paraffins are cheap and widely used, but the flame retardancy and plasticizing properties of chlorinated paraffins are not very good, so improving the flame retardancy and plasticizing properties of chlorinated paraffins is a hot topic in the plastic processing industry.
It has been found that the flame retardant plasticizer tricresyl phosphate (TCP) can improve the compatibility and flame retardancy of chlorinated paraffin and materials, but its price is expensive and its application cost is high, so it is limited to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diisopropyl phenylphosphinate flame retardant composition and application method thereof
  • Diisopropyl phenylphosphinate flame retardant composition and application method thereof
  • Diisopropyl phenylphosphinate flame retardant composition and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1 Add different proportions of PPDI and CP52 to polyvinyl chloride, stir evenly, extrude a sample strip with a diameter of about 3 mm at melting temperature with an XJ-01 extruder, and measure its The limiting oxygen index, the results are shown in Table 2.

[0030] Table 2 Flame retardant data of PVC compounded by flame retardant PPDI and CP52

[0031]

Embodiment 2

[0032] Example 2 Add different proportions of PPDI, CP52 and STCE to polyvinyl chloride, stir evenly, extrude a sample strip with a diameter of about 3mm at the melting temperature with an XJ-01 extruder, and use a HC900-2 oxygen index tester The limiting oxygen index was measured, and the results are shown in Table 3.

[0033] Table 3 Flame retardant data of PVC compounded by flame retardant PPDI, CP52 and STCE

[0034]

Embodiment 3

[0035] Example 3 Add different proportions of PPDI, CP52 and STDE to polyvinyl chloride, stir evenly, use XJ-01 extruder to extrude a sample with a diameter of about 3mm at the melting temperature, and use HC900-2 oxygen index tester Measure its limiting oxygen index, and the results are shown in Table 4.

[0036] Table 4 Flame retardant data of PVC compounded by flame retardant PPDI, CP52 and STDE

[0037]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a diisopropyl phenylphosphinate (PPDI) flame retardant composition and an application method thereof. The flame retardant composition is prepared by the steps of compounding one or two of PPDI, chlorinated paraffin-52 (short for CP52), tetrachloroethyl silicate (short for STCE), tetradichloropropyl silicate (short for STDE) or tridichloropropyl phenyl silicate (short for STDPE) according to any ratio, and then, uniformly mixing, wherein the weight parts of both PPDI and CP52 are larger than zero. The flame retardant composition provided by the invention has the advantages of synergistic effect among various elements, good compatibility with materials, high flame-retardant efficiency, low cost and the like and can be used as a flame retardant for materials such as polyvinyl chloride, polyurethane, unsaturated resin, epoxy resin and the like so as to have favorable application prospects.

Description

technical field [0001] The invention relates to a flame retardant composition of diisopropyl phenylphosphinate and an application method thereof. The flame retardant composition can be used as a flame retardant for polyvinyl chloride, polyurethane, unsaturated resin, epoxy resin and other materials. Fuel. Background technique [0002] With the rapid development of the polymer material processing industry, there is a great demand for flame retardant plasticizers. Chlorinated paraffins are cheap and widely used, but the flame retardancy and plasticizing properties of chlorinated paraffins are not very good. Therefore, improving the flame retardancy and plasticizing properties of chlorinated paraffins is a hot topic in the plastic processing industry. It has been found that the flame retardant plasticizer tricresyl phosphate (TCP) can improve the compatibility and flame retardancy of chlorinated paraffin and materials, but it is expensive and has high application costs, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/00C08K5/5313C08K5/02C08K5/5415C08L27/06
Inventor 刘垚俞春雷王彦林
Owner RES INST OF XIANGCHENG SUZHOU UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products