A kind of far-infrared ceramic material

A ceramic material and far-infrared technology, applied in the field of ceramic materials, can solve problems such as poisoning, affecting human health, endangering physical and mental health, etc., and achieve the effects of improving blood circulation, obvious medical and health care effects, and increasing immunity.

Active Publication Date: 2019-12-03
南通东昌环保设备科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many harmful elements in colored glaze, such as lead, mercury, cadmium, etc., which affect human health.
If unqualified ceramic products are used for a long time, the harmful elements in the glaze will dissolve and enter the human body with food, which will gradually cause poisoning
At the same time, ceramic products such as floor tiles are highly radioactive, which seriously endangers people's physical and mental health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A far-infrared ceramic material made of the following raw materials: medical stone powder 70%, paraffin wax 9%, food-grade polypropylene copolymer 3%, organotin stabilizer 1.5%, jade powder 1.5%, nano-titanium dioxide 1.5%, Calcium borate 13.5%.

[0022] The preparation method of the far-infrared ceramic material is as follows:

[0023] a. Weigh 70KG of medical stone powder, 13.5KG of calcium borate, 1.5KG of jade powder and 1.5KG of nano-titanium dioxide, grind and pulverize respectively, and sieve to form raw material powder of 2000 mesh, and set aside.

[0024] b. Put 9KG of paraffin wax, 3KG of food-grade polypropylene copolymer, and 1.5KG of organic tin stabilizer into the mixer, and heat to 200°C to dissolve them into liquid, and stir evenly.

[0025] c. Put the medical stone powder and calcium borate raw material powder described in step a into the mixer in step b and stir for two hours to make the raw materials mix evenly.

[0026] d. Put the jade powder and n...

Embodiment 2

[0028] A far-infrared ceramic material made of the following raw materials: medical stone powder 65%, paraffin wax 11%, food-grade polypropylene copolymer 4%, organotin stabilizer 2%, jade powder 2%, nano-titanium dioxide 2%, Calcium borate 14%.

[0029] The preparation method of the far-infrared ceramic material is as follows:

[0030] a. Weigh 65KG of medical stone powder, 14KG of calcium borate, 2KG of jade powder and 2KG of nano-titanium dioxide, grind and pulverize respectively, and sieve to form raw material powder of 2000 mesh, and set aside.

[0031] b. Put 11KG of paraffin wax, 4KG of food-grade polypropylene copolymer and 2KG of organotin stabilizer into the mixer, and heat it to 200°C to dissolve it into a liquid, and stir evenly.

[0032] c. Put the medical stone powder and calcium borate raw material powder described in step a into the mixer in step b and stir for two hours to make the raw materials mix evenly.

[0033] d. Put the jade powder and nano-titanium d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vicat softening pointaaaaaaaaaa
Login to View More

Abstract

A far-infrared ceramic material is prepared from medical stone powder, paraffin, food-grade polypropylene copolymer, an organic tin stabilizer, jade powder, nano titanium dioxide and calcium borate. A preparation method of the far-infrared ceramic material includes: a, weighing medical stone powder, calcium borate, jade powder and nano titanium dioxide, respectively grinding and screening to form 2000-mesh raw material powder for standby application; b, adding paraffin, food-grade polypropylene copolymer and organic tin stabilizer into a stirrer, heating to 200 DEG C, melting into liquid, and well stirring; c, well stirring medical stone powder and calcium borate raw material powder at the step a in the stirrer; d, sequentially adding jade powder and nano titanium dioxide raw material powder at the step a into the stirrer, and well stirring. The far-infrared ceramic material is capable of improving human blood circulation, reducing blood acidity, promoting metabolism and improving immunity and has an evident medical healthcare effect on hypertension, hyperlipidemia and rheumatoid arthritis.

Description

technical field [0001] The invention belongs to the technical field of ceramic materials, and in particular relates to a far-infrared ceramic material. Background technique [0002] With the improvement of people's living standards, the demand for the living environment is getting higher and higher. While requiring comfort, more attention is paid to the impact of the environment on human health. At present, most of the materials used in jewelry and watches are gold, silver, steel, iron, plastic and other materials, which are not only not beneficial to the human body, but also have complicated manufacturing processes and high costs. In recent years, some similar products have appeared on the market, such as zirconia ceramics. Zirconia ceramic watches only have the gloss and beauty of the appearance, but still have no other functions. Ceramic products are widely concerned as indoor and outdoor decorations, and people's requirements for ceramic products are getting higher and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/18C04B35/632C04B35/634
CPCC04B35/18C04B35/6325C04B35/63408C04B2235/3208C04B2235/3232C04B2235/3409C04B2235/3427
Inventor 蔡彦娟
Owner 南通东昌环保设备科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com