Waterproof wearing-resistant building coating and preparation method thereof

A technology of architectural coatings and waterproofing agents, applied in the field of coatings, can solve the problems of poor waterproof performance and non-wear resistance, achieve high waterproof grade, strong wear resistance, and solve the effect of poor waterproof performance

Inactive Publication Date: 2018-02-23
FOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above deficiencies in the prior art, the object of the present invention is to provide a waterproof and wear-resistant architectural coating and its preparation method, aiming to solve the problem of poor waterproof performance and non-wear resistance of existing coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The waterproof and wear-resistant architectural coating of the present invention consists of the following components in parts by weight:

[0047] 45 parts of plant fiber;

[0048] 1 part of nano mica;

[0049] 5 parts of quartz monzonite;

[0050] 7 parts of film-forming agent;

[0051] 8 parts of dispersant;

[0052] 30 parts of water;

[0053] 3 parts of thickener;

[0054] 5 parts of anti-wear agent;

[0055] 3 parts of waterproofing agent;

[0056] The preparation method of the waterproof and wear-resistant architectural coating of the present invention is as follows: when preparing, add the above-mentioned plant fiber, nano-mica, quartz monzonite, film-forming agent, and dispersant into water and stir for 2 minutes, heat up to 60 ° C, and then Add thickener, waterproofing agent, wear-resistant agent, stir for 1min, cool to room temperature and make.

Embodiment 2

[0058] The waterproof and wear-resistant architectural coating of the present invention consists of the following components in parts by weight:

[0059] 60 parts of plant fiber;

[0060] 3 parts of nano mica;

[0061] 8 parts of quartz monzonite;

[0062] 12 parts of film-forming agent;

[0063] 12 parts of dispersant;

[0064] 90 parts of water;

[0065] 5 parts of thickener;

[0066] 8 parts of anti-wear agent;

[0067] 5 parts of waterproofing agent;

[0068] The preparation method of the waterproof and wear-resistant architectural coating of the present invention is as follows: when preparing, add the above-mentioned plant fiber, nano-mica, quartz monzonite, film-forming agent, and dispersant into water and stir for 6 minutes, heat up to 70 ° C, and then Add thickener, waterproofing agent, wear-resistant agent, stir for 1min, cool to room temperature and make.

Embodiment 3

[0070] The waterproof and wear-resistant architectural coating of the present invention consists of the following components in parts by weight:

[0071] 50 parts of plant fiber;

[0072] 2 parts of nano mica;

[0073] 6 parts of quartz monzonite;

[0074] 10 parts of film-forming agent;

[0075] 10 parts of dispersant;

[0076] 60 parts of water;

[0077] 4 parts of thickener;

[0078] 7 parts of anti-wear agent;

[0079] 4 parts of waterproofing agent;

[0080] The preparation method of the waterproof and wear-resistant architectural coating of the present invention is as follows: when preparing, add the above-mentioned plant fiber, nano-mica, quartz monzonite, film-forming agent, and dispersant into water and stir for 10 minutes, heat up to 80° C., and then Add thickener, waterproofing agent, wear-resistant agent, stir for 1min, cool to room temperature and make.

[0081] According to the performance test, the wear-resistant and waterproof coating prepared by the pres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof wearing-resistant building coating and a preparation method thereof. The waterproof wearing-resistant building coating comprises the following components in partsby weight: 45-60 parts of a plant fiber, 1-3 parts of nano mica, 5-8 parts of medical stone, 7-12 parts of a film-forming agent, 8-12 parts of a dispersing agent, 30-90 parts of water, 3-5 parts of athickening agent, 5-8 parts of a wearing resistant agent and 3-5 parts of a waterproof agent. The coating prepared according to the formula has the characteristics of being good in waterproof propertyand wearing resistance, and the coating formed on the surface of a building wall is not only smooth in surface and good in wearing resistance, but also high in waterproof grade, is particularly applicable to building walls in wet environments such as seaside, and meanwhile is low in cost and simple in preparation method. In addition, as the constitution components of the coating are mostly natural substances or extracts thereof, the coating is free of environment pollution, beneficial to human body health and very good in market prospect.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a waterproof and wear-resistant architectural coating and a preparation method thereof. Background technique [0002] At present, the exterior walls of buildings are generally painted with paint, which can be well bonded to the base material and form a complete and tough protective film when painted on the surface of the object. Architectural paints have decorative, protective, and habitability-improving functions. The proportions of various functions vary depending on the purpose of use. The decorative function is to improve the appearance value of a building by beautifying it. The current architectural coatings are mainly made of film-forming agents, dispersants, thickeners, plant fibers, stone powder and other materials. The formula contains granular substances. After the film is formed, these granular substances are dispersed on the surface to form unevenness. The rough surface of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): C09D197/02C09D7/61C09D7/63C09D7/65
CPCC09D197/02C08K2201/011
Inventor陈强
OwnerFOSHAN CITY SANSHUI DISTRICT MANYA ENVIRONMENTAL PROTECTION TECH CO LTD