A flame-retardant anti-virus anti-chemical fabric and its manufacturing method

A manufacturing method and fabric technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., to achieve excellent protection ability, wide application and market prospects, good anti-toxicity and anti-hazardous chemical permeability Effect

Active Publication Date: 2021-05-28
北京邦维高科新材料科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It can be seen from the above that at present, the research and development of chemical protective fabrics at home and abroad have not yet involved protective fabrics with integrated flame-retardant, anti-virus and chemical-resistant functions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A flame-retardant anti-virus anti-chemical fabric and its manufacturing method
  • A flame-retardant anti-virus anti-chemical fabric and its manufacturing method
  • A flame-retardant anti-virus anti-chemical fabric and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The first step, the preparation of the outer layer 1;

[0039] Fully mix polyolefin resin and polyolefin flame retardant at a weight ratio of 100:5-30 to obtain a mixed raw material; then extrude the mixed raw material through a film blowing machine or a casting machine, and the extrusion temperature is 160-220°C. The extrusion speed is 5-30m / min to obtain the outer layer 1;

[0040] The polyolefin flame retardant is decabromodiphenyl ether, ammonium polyphosphate or phosphoric acid ester;

[0041] The second step, the preparation of the middle layer;

[0042] (1) Preparation of flame-retardant fabric-21: using at least one of flame-retardant polyester fiber, flame-retardant acrylic fiber, flame-retardant vinylon or flame-retardant nylon to obtain flame-retardant fabric-21 through a weaving process;

[0043] (2) Preparation of flame-retardant fabric 222: using at least one of flame-retardant viscose fiber, para-aramid fiber, meta-aramid fiber, polyarylene oxadiazole f...

Embodiment 1

[0061] A flame-retardant, anti-virus and chemical-resistant fabric is characterized in that the fabric includes an outer layer 1, a middle layer and an inner layer 3 from the outside to the inside, and its structure is as follows: figure 1 shown;

[0062] The outer layer 1 is made of 100 parts by weight polyolefin resin and 6 parts by weight polyolefin flame retardant blended blown film, and the polyolefin resin is blended by 100 parts by weight linear low density polyethylene resin and 50 parts by weight polyolefin plastomer resin Composition, the flame retardant is decabromodiphenyl ether, the extrusion temperature is 170°C, and the extrusion speed is 5m / min to obtain the outer layer 1.

[0063] The middle layer is made of flame-retardant fabric 1 21, flame-retardant fabric 2 22 and polyhalogenated olefin film 23 by compounding, and the structure is arranged from outside to inside as flame-retardant fabric 1 21 / flame-retardant fabric 2 22 / polyhalogen Olefin film 23; fla...

Embodiment 2

[0068] A flame-retardant, anti-virus and chemical-resistant fabric is characterized in that the fabric includes an outer layer 1, a middle layer and an inner layer 3 from the outside to the inside, and its structure is as follows: figure 2 shown;

[0069] The outer layer 1 is made of 100 parts by weight of polyolefin resin and 28 parts by weight of polyolefin flame retardant blended blown film, and the polyolefin resin is composed of 100 parts by weight of low density polyethylene resin and 100 parts by weight of polypropylene homopolymer resin , the flame retardant is ammonium polyphosphate, the extrusion temperature is 195°C, and the extrusion speed is 25m / min to obtain the outer layer 1.

[0070] The middle layer is made of flame-retardant fabric 1 21, flame-retardant fabric 2 22 and polyhalogenated olefin film 23 by compounding, and the structure is arranged from outside to inside as flame-retardant fabric 2 22 / flame-retardant fabric 1 21 / polyhalogenated Olefin film 23; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Basis weightaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant anti-virus anti-chemical fabric and a manufacturing method thereof. The fabric includes an outer layer, a middle layer and an inner layer from the outside to the inside, and the layers are connected in sequence; the outer layer is made of flame-retardant polyolefin film; the inner layer is made of ePTFE film, flame-retardant TPU film, flame-retardant Any one of TPEE film, flame retardant PVC film, flame retardant polyolefin film, flame retardant PU coating, flame retardant PVC coating, PVDC coating or PVDF coating; the middle layer is made of flame retardant fiber fabric and polyester Composed of halogenated olefin film; the fabric has excellent anti-hazardous chemical permeability, good anti-toxicity and flame retardancy, and is light and thin. The overall thickness of the fabric is 1.0‑2.5mm, and the weight is less than 550g / m 2 , Anti-mustard gas penetration time ≥ 72h, anti-chemical penetration time ≥ 8h, after-burning ≤ 10s, smoldering ≤ 10s, damage length ≤ 100mm. The process of the method is simple and easy.

Description

technical field [0001] The invention relates to the field of chemical protective fabrics, in particular to a flame-retardant, anti-virus and chemical-resistant fabric and a manufacturing method thereof. Background technique [0002] Chemical protective clothing is the main equipment to protect the life safety of on-site emergency rescue personnel when dealing with hazardous chemical accidents, and its core component is chemical protective fabric. Moreover, the phenomenon of hazardous chemical accidents is often accompanied by some flash and deflagration phenomena, so the flame retardancy of chemical protective fabrics is also required. Therefore, it is especially necessary to endow the chemical protective fabric with anti-virus function. [0003] Traditional chemical protection fabrics are formed by coating rubber materials on base fabrics, which have good chemical resistance properties. However, the protective function of a single rubber material is limited. Generally, a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/02B32B27/08B32B27/32B32B27/30B32B33/00B32B7/12B32B27/36B32B27/28B32B27/40B32B37/12B32B37/15B32B38/00
Inventor 张杰张婷婷陈祯田新宇任玮霍晓兵
Owner 北京邦维高科新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap