Fabricated aluminum-calcium composite board material as well as preparation method and application thereof

A composite board, prefabricated technology, used in covering/lining, construction, building structure, etc., can solve the problems of degumming, inability to adjust the size, etc., to achieve the effect of improving the assembly rate, accurate size, and not easy to deform

Active Publication Date: 2021-06-01
湖北星立方科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that adhesives are often used in the preparation of aluminum-calcium composite board materials in the prior art, and there is a risk of degumming during use; in addition, aluminum materials are used directly in the prior art without additional treatment. The size cannot be adjusted flexibly according to different occasions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabricated aluminum-calcium composite board material as well as preparation method and application thereof
  • Fabricated aluminum-calcium composite board material as well as preparation method and application thereof
  • Fabricated aluminum-calcium composite board material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] An assembled aluminum-calcium composite board material, the aluminum-calcium composite board material is composed of calcium material and aluminum material, and the calcium material contains raw materials with the following weight:

[0046]

[0047] The modifier comprises raw materials by weight of:

[0048]

[0049] Further, the preparation method of the aluminum material includes the following steps:

[0050] (1) Cut the aluminum profiles into small sections and weld them into a rectangular aluminum frame;

[0051] (2) Fix the aluminum rod inside the rectangular aluminum frame to strengthen the strength of the aluminum frame and improve its deformation degree.

[0052] The present invention also provides a method for preparing the above-mentioned assembled aluminum-calcium composite board material, the preparation method comprising the following steps:

[0053] (1) Preparation of latex liquid: redispersible latex powder and water are prepared in proportion, an...

Embodiment 2

[0065] An assembled aluminum-calcium composite board material, the aluminum-calcium composite board material is composed of calcium material and aluminum material, and the calcium material contains raw materials with the following weight:

[0066]

[0067] The modifier comprises raw materials by weight of:

[0068]

[0069] Further, the preparation method of the aluminum material includes the following steps:

[0070] (1) Cut the aluminum profiles into small sections and weld them into a rectangular aluminum frame;

[0071] (2) Fix the aluminum rod inside the rectangular aluminum frame to strengthen the strength of the aluminum frame and improve its deformation degree.

[0072] The present invention also provides a method for preparing the above-mentioned assembled aluminum-calcium composite board material, the preparation method comprising the following steps:

[0073] (1) Preparation of latex liquid: redispersible latex powder and water are prepared in proportion, an...

Embodiment 3

[0085] An assembled aluminum-calcium composite board material, the aluminum-calcium composite board material is composed of calcium material and aluminum material, and the calcium material contains raw materials with the following weight:

[0086]

[0087]

[0088] The modifier comprises raw materials by weight of:

[0089]

[0090] Further, the preparation method of the aluminum material includes the following steps:

[0091] (1) Cut the aluminum profiles into small sections and weld them into a rectangular aluminum frame;

[0092] (2) Fix the aluminum rod inside the rectangular aluminum frame to strengthen the strength of the aluminum frame and improve its deformation degree.

[0093] The present invention also provides a method for preparing the above-mentioned assembled aluminum-calcium composite board material, the preparation method comprising the following steps:

[0094] (1) Preparation of latex liquid: redispersible latex powder and water are prepared in pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
densityaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fabricated aluminum-calcium composite board material, which is characterized in that an outer frame of a board is an aluminum bar reinforced aluminum profile, a main body is a modified calcium material, and the calcium material is composed of calcium sulfate hemihydrate powder, white Portland cement, kaolin, expanded perlite particles, an auxiliary material, a modifier and the like. The material is prepared through the main steps of stirring hydration, mold bottom surface pouring, mold whole pouring, demolding polishing, drying and the like, the obtained product fully combines the advantages of an inorganic mineral material and a metal material, is suitable for manufacturing facing materials such as suspended ceilings, wallboards and background walls, and is beneficial to fabricated construction of building decoration. The invention further discloses a preparation method of the fabricated aluminum-calcium composite board material and application of the fabricated aluminum-calcium composite board material in fabricated construction of building decoration.

Description

technical field [0001] The present invention relates to the field of architectural decoration, in particular to an assembled aluminum-calcium composite board material, to a method for preparing the assembled aluminum-calcium composite board material, and to the application of the assembled aluminum-calcium composite board material in the assembled construction of architectural decoration application. Background technique [0002] The current decorative panels are mainly divided into inorganic materials and organic materials. In the construction of large-scale projects, due to the needs of fire protection, the fire protection level of decorative materials is often required to reach the flame-retardant or non-combustible level. Therefore, inorganic materials have become the mainstream used in decorative panels. Material. [0003] Inorganic materials are mainly divided into inorganic mineral materials and metal materials. Inorganic mineral materials mainly include gypsum board...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14E04F13/072
CPCC04B28/145E04F13/08C04B7/02C04B14/106C04B14/185C04B14/42C04B2103/0057C04B2103/65C04B2103/32C04B24/003Y02W30/91
Inventor 李俊
Owner 湖北星立方科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com