Post-processing method for improving 3D printing rock mass performance

A technology of 3D printing and rock printing, applied in 3D object support structures, metal processing equipment, manufacturing tools, etc., can solve the problem of low fluidity of epoxy resin, and achieve the effect of eliminating the defect of delamination

Pending Publication Date: 2022-04-01
CHANGAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the low fluidity of epoxy resin and the initial curing in a short period of time, how to use epoxy resin to post-process 3D printed rock mass is a key issue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Post-processing method for improving 3D printing rock mass performance
  • Post-processing method for improving 3D printing rock mass performance
  • Post-processing method for improving 3D printing rock mass performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention. The test methods for which specific conditions are not indicated in the following examples are usually in accordance with conventional conditions, or in accordance with the conditions suggested by each manufacturer.

[0035] The invention provides a post-processing method for improving the performance of 3D printed rock mass, comprising the following steps:

[0036] Step 1, defoaming the modified epoxy resin solution to obtain the defoamed modified epoxy resin solution, and putting the defoamed modified epoxy resin solution into a sealed bucket to pump air;

[0037] Specifically, the modified epoxy ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of geotechnical engineering, and particularly relates to a post-processing method for improving the performance of a 3D printing rock mass. Comprising the following steps: step 1, defoaming a modified epoxy resin solution to obtain a defoamed modified epoxy resin solution, and putting the defoamed modified epoxy resin solution into a sealing barrel for air exhaust; step 2, weighing a 3D printing rock mass sample, drying the 3D printing rock mass sample at a constant temperature to obtain a dried 3D printing rock mass sample, adding the dried 3D printing rock mass sample into a sealing barrel, and immersing the dried 3D printing rock mass sample in the defoamed modified epoxy resin solution to obtain a first mixture; and step 3, sequentially vacuumizing, standing and drying the first mixture to obtain the improved 3D printing rock mass sample. The 3D printing rock mass sample with various mechanical properties highly similar to those of a natural rock mass is manufactured, the result reliability of the 3D printing rock mass replacing the natural rock mass for an indoor test is improved, and a new method is provided for manually restoring the natural rock mass.

Description

technical field [0001] The invention belongs to the technical field of geotechnical engineering, and in particular relates to a post-processing method for improving the performance of 3D printed rock mass. Background technique [0002] Transparent 3D printing technology has been proved to be a powerful method for the preparation of samples with complex structures. This technology has attracted widespread attention and application in many fields, and its advantages have been applied in the field of fractured rock mass. 3D printing technology can be used to quickly print rock mass samples with internal defects, and can ensure a high degree of consistency between samples, which solves the problem of micro-cracks in natural rocks when making prefabricated fissures, low precision of prefabricated fissures, and prefabricated fissures. Make difficult questions. [0003] Different from the pressing, forging, casting and other methods used in traditional molding technology, the prin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C64/379B29C64/141B33Y40/20B33Y10/00
Inventor 田威余宸王肖辉高晋峰郭健云伟
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap