Colorful reflective fabric and preparation method thereof

A reflective and fabric technology, which is applied in the field of colorful reflective fabric and its preparation, can solve the problems of insufficient strength of the fabric, and achieve the effect of guaranteed effect and high strength

Pending Publication Date: 2022-08-02
石狮市晓光服饰反光材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this comparison document, the base material is firstly bonded with microbeads, and the method of coating is carried out, but the strength of the fabric obtained by vegetation in this way is insufficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful reflective fabric and preparation method thereof
  • Colorful reflective fabric and preparation method thereof
  • Colorful reflective fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0042] see figure 1 , a colorful reflective fabric, the colorful reflective fabric from top to bottom includes:

[0043] Reflective layer 1;

[0044] The reflective layer is prepared from a reflective microbead layer 111 , a protective adhesive layer 12 and a PE film (not marked in the figure); the thickness of the reflective microbead layer is 3-10 μm. It should be further noted that the thickness of the reflective microbead layer can be the particle size of the reflective microbeads, or microbeads with different particle sizes can be selected to stack the reflective microbead layers according to requirements, thereby improving the reflection effect. The thickness of the protective adhesive layer 12 is 1-2 μm.

[0045] Zinc sulfide layer 2; the thickness of the zinc sulfide layer is 1-2 μm. It should be further explained that when light is irradiated on the surface of the microbeads, due to the high refraction effect of the microbeads, the light will be concentrated on the ...

Embodiment 2

[0061] The difference between this embodiment and Embodiment 1 is:

[0062] The components of the protective glue are: polyurethane resin: 20kg; ethyl acetate: 55kg; curing agent: 2kg; organosiloxane leveling agent: 60g.

Embodiment 3

[0064] The difference between this embodiment and Embodiment 1 is:

[0065] The components of the protective glue are: polyurethane resin: 10kg; ethyl acetate: 40kg; curing agent: 1kg; organosiloxane leveling agent: 40g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colorful reflective fabric and a preparation method thereof, and belongs to the technical field of special garment fabrics. The colorful reflective fabric comprises, from top to bottom, a reflective layer; the reflective layer is prepared from a reflective microbead layer, a protective adhesive layer and a PE film; a zinc sulfide layer; the composite adhesive layer can be used for bonding a substrate; the colorful reflective fabric provided by the invention not only can overcome the defect that the traditional surface cannot present colorful colors, but also can make up the defect that the glue limits the low retroreflection coefficient of the glass beads, and has wider application. The fabric is high in strength, after a zinc sulfide layer is evaporated on a glass bead body in a traditional technology, glue of the glass bead needs to be removed through water washing, and the situation that the strength of the fabric is further affected due to the fact that the retroreflection coefficient is increased by the glue is avoided; and the effect can be ensured without removal.

Description

technical field [0001] The invention relates to the technical field of special clothing fabrics, in particular to a colorful reflective fabric and a preparation method thereof. Background technique [0002] Colorful reflective fabric, as the name implies, is different from the reflective effect of conventional aluminum mirrors. Under the effect of lighting, the reflective fabric presents colorful effects (red, orange, yellow, green, blue, blue and purple) with different angles, and the application is more extensive and diverse. Colorful reflective fabrics can be prepared with colorful reflective effects on the surface according to different substrates, such as: luggage fabrics and other clothing fabrics with different properties or shoe materials, etc., which have a wide range of adaptability. [0003] High-refractive-index glass beads are widely used in reflective materials and road markings. Simply using high-refractive-index glass beads will not have an ideal reflective e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/21C09J175/04C09J11/06C09J11/08C23C14/06C23C14/24
CPCC09J7/21C09J175/04C09J11/06C09J11/08C23C14/0629C23C14/24C09J2400/263C08L83/04C08K5/101Y02E10/52
Inventor 王凯斌刘华奇吴文渊
Owner 石狮市晓光服饰反光材料有限公司