Elastomeric shaft seal formed without oven post curing

a technology of elastomeric shaft and oven post, which is applied in the field of elastomeric shaft seals, can solve the problems of significant capital investment, labor cost, energy consumption, and other burdens on the manufacturer, and achieve the effect of reducing capital investment in oven post curing equipment, labor cost of performing oven post curing step, and exceptional physical properties

Inactive Publication Date: 2015-10-01
FEDERAL MOGUL MOTORPARTS LLC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The invention eliminates a step called "oven post curing" which saves money and energy. It also improves the physical properties of the elastomeric seal produced without this step.

Problems solved by technology

Thus, the oven post curing step involves significant capital investment, labor costs, energy consumption, and other burdens on a manufacturer of the elastomeric seals.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Elastomeric shaft seal formed without oven post curing
  • Elastomeric shaft seal formed without oven post curing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013]One aspect of the invention provides a method of forming an elastomeric seal 20, for example the elastomeric seal 20 shown in FIGS. 1 and 2, for sealing and protecting a metal shaft (not shown) of an automotive vehicle application from oil and debris. The elastomeric seal 20 includes an elastomeric compound 22, including a fluoroelastomer (FKM), chemically coupled to a metal sealing ring 24. The method of forming the elastomeric seal 20 includes chemically coupling the elastomeric compound 22 to the metal sealing ring 24 during a molding step and does not require an oven post curing step. By eliminating the oven post curing step, capital investment, labor costs, and energy consumed is significantly reduced, compared to methods of forming elastomeric seals of the prior art requiring an oven post curing step.

[0014]The method of forming the elastomeric seal 20 without the oven post curing step first includes providing the elastomeric compound 22. In one preferred embodiment, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

An elastomeric seal (20), such as a shaft seal for automotive vehicle applications, includes an elastomeric compound (22) chemically coupled to a metal sealing ring (24) and is formed without an oven post curing step. The elastomeric seal (20) provides exceptional physical properties, similar to those of elastomeric seals of the prior art formed with an oven post curing step. The elastomeric seal (20) has an elastic modulus of 6.0 MPa to 13.0 MPa and a tensile strength of 11.1 MPa to 14.8 MPa. The elastomeric compound (22) includes 52.0 to 68.0 wt. % fluoroelastomer, 20.0 to 35.0 wt. % calcium silicate, and 5.0 to 15.0 wt. % diatomite. The elastomeric compound (22) is fully cured and chemically coupled to the metal sealing ring (24) during the compression or injection molding step, and thus an oven post curing step is not required.

Description

[0001]This divisional patent application claims priority to U.S. Utility application Ser. No. 13 / 748,752, filed Jan. 24, 2013, and is incorporated herein by reference.BACKGROUND OF THE INVENTION[0002]1. Field of the Invention[0003]This invention relates to elastomeric seals, such as shaft seals for automotive vehicle applications, and methods of forming the elastomeric seals.[0004]2. Related Art[0005]Elastomeric seals, such as shaft seals for automotive vehicle applications, typically include an elastomeric compound chemically coupled to a metal sealing ring. The elastomeric compound can include a variety of elastomers, polymers, and fillers, such as polyacrylates, ethylene acrylic, and fluoroelastomers. Examples of such elastomeric seals are provided by Federal-Mogul Corporation.[0006]The elastomeric seals of the prior art are formed by molding the elastomeric compound to the metal sealing ring, and then oven post curing the elastomeric seal after the molding step to fully cure and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): F16J15/16C08K13/02B29C45/00B29C43/20B29C45/16B29C43/00B29C43/02B29C43/18C08J5/00B29C45/14
CPCF16J15/16B29K2705/00C08K13/02B29C45/0001B29C45/14336B29C45/1459B29C45/1671B29C43/003B29C43/027B29C43/18B29C43/203C08J2327/20B29C2045/14459B29C2045/14868B29C2043/181B29L2009/003B29L2031/265B29K2027/12B29K2105/253C08J5/00B29D99/0053B32B15/082F16J15/122B29K2827/12B29D99/0085F16J15/121B32B27/20B32B1/08B32B2264/102B32B2264/108B32B2307/51B32B2307/54B32B2581/00B29C65/405F16J15/12
Inventor BIAN, JUNFENGHOLLIDAY, ROGERTRIPATHY, BHAWANI
Owner FEDERAL MOGUL MOTORPARTS LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com