Cordierite-doped non-chromate Dacromet coating and preparation method

A cordierite and coating technology, used in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of low strength and poor wear resistance, and achieve increased strength and wear resistance, and the coating is dense and smooth. , the effect of reducing production costs

CN107163787AInactive Publication Date: 2017-09-15合肥新意境材料有限责任公司
3 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2017-09-15
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention discloses a cordierite-doped non-chromate Dacromet coating and a preparation method thereof, the non-chromate Dacromet coating is characterized by comprising the following parts by weight of raw materials: 3-5 parts of cordierite, 3-5 parts of corundum powder, 4-8 parts of silicon carbide, 1-3 parts of fly ash, 5-10 parts of polytetrafluoroethylene powder, 10-15 parts of epoxy resin E42, 10-15 parts of vinyl triamine, 1-2 parts of diatomite, 20-30 parts of zinc powder, 20-30 parts of aluminum powder, 40-50 parts of silane coupling agent KH550, 5-10 parts of ethanol, 50-70 parts of acetone and 0.3-0.6 part of polydimethylsiloxane; the non-chromate Dacromet coating has the advantages of high strength and wear resistance and good liquidity and adhesion, a formed coating is dense and smooth, the defects of low strength and poor wear resistance of a Dacromet coating solution can be solved, the non-chromate Dacromet coating is highly competitive in the market; the cordierite,the fly ash and the like are added for cooperation to reduce the production cost in the premise of no influence on the property of the coating.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a dacromet paint, which belongs to the field of metal anticorrosion, in particular to a cordierite-doped chrome-free dacromet paint and a preparation method thereof. Background technique

[0002] Corrosion of steel directly leads to a large number of accidents or hidden dangers of accidents every year, causing huge economic losses and seriously affecting national economic development and security. How to provide durable corrosion resistance has become a research hotspot. Dacromet coating is a metal anti-corrosion coating composed of scaly zinc powder, aluminum powder chromic anhydride and organic reducing agent. It has been widely used due to its strong corrosion resistance, high temperature resistance, and high permeability. However, , because the Dacromet treatment solution contains about 2% of highly carcinogenic and highly toxic Cr 6+ . Therefore, the current Dacromet coating has the disadvantages of being not environmen...

Examples

Embodiment

[0018] A kind of cordierite-doped chrome-free dacromet coating, is characterized in that, is made from the raw material of following weight part:

[0019] Cordierite 5, corundum powder 5, silicon carbide 8, fly ash 3, polytetrafluoroethylene powder 10, epoxy resin E42 15, vinyltriamine 15, diatomaceous earth 2, zinc powder 30, aluminum powder 30, silane Coupling agent KH550 50, ethanol 10, acetone 70, polydimethylsiloxane 0.6;

[0020] The zinc powder and aluminum powder are flake powders.

[0021] A kind of cordierite-doped chrome-free dacromet paint and preparation method thereof, is characterized in that, comprises the following operation steps:

[0022] a. ultrasonically disperse corundum powder with ethanol solution for 1-2 hours, filter and dry;

[0023] b. Grind the corundum powder obtained in step a, cordierite, silicon carbide, fly ash, polytetrafluoroethylene powder and diatomaceous earth in a mortar to make it fully mixed, then transfer it to a crucible, place it ...