Double-refraction optical film, elliptic polarizing piece using same, and liquid crystal display using said polarizing piece

A liquid crystal display, elliptical polarization technology, applied in optics, optical components, polarizing components, etc., can solve the problems of small photoelastic coefficient, difficult to provide and so on

Inactive Publication Date: 2008-11-26
NITTO DENKO CORP
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] That is, it is difficult for any conventional technology to provide a high degree of orientation (in order to obtain the desired retardation value) and a small photoelastic coefficient (in order to withstand the heat and / or moisture application during the durability test). Irregularities that reduce contrast) birefringent film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-refraction optical film, elliptic polarizing piece using same, and liquid crystal display using said polarizing piece
  • Double-refraction optical film, elliptic polarizing piece using same, and liquid crystal display using said polarizing piece
  • Double-refraction optical film, elliptic polarizing piece using same, and liquid crystal display using said polarizing piece

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] There is no particular limitation on the production method of the birefringent optical film of the present invention. For example, it can be produced by coating the polymer material of the present invention on a base film or the like. At this point, the polymer material can be heated to melt. It is also possible to dissolve in a solvent to obtain a polymer solution, and then apply the solution. From the viewpoints of production efficiency and control of optical anisotropy, it is preferable to coat a polymer solution. When a polymer solution is used, from the viewpoint of its viscosity or the like, for example, it is preferable to contain 5-50 parts by weight, more preferably 10-40 parts by weight of the polymer material per 100 parts by weight of the solvent.

[0029] In a method of coating a polymer solution on a base film or the like, the base film can be used as the polymer layer of the present invention. For example, a polymer layer is made by coating a polymer s...

Embodiment 1

[0133] Polyimide is dissolved in methyl isobutyl ketone to make 15% by weight solution, the Mw=120,000 of described polyimide, it is made of 2,2-two (3,4-dicarboxylic acid phenyl ) Hexafluoropropane dianhydride (6FDA) and 2,2'-bis(trifluoromethyl)-4,4'-diaminobiphenyl (PFMB or TFMB). This solution was coated on a 40 μm thick thermoplastic polymer base film (trade name: ZEONOR, manufactured by Nippon Zeon Co. Ltd), followed by drying at 150° C., thereby obtaining a laminated birefringent optical film having nx = ny > nz optical anisotropy. When measured, the photoelastic coefficient of the polymer base film was 4 × 10 -8 cm 2 / N, while the photoelastic coefficient of the 6FDA-PFMB layer (thickness d=7.2μm) is 98×10 -8 cm 2 / N. Therefore, the birefringent optical film thus produced has a calculated value of Σ(Cn×Wn) of 18×10 -8 cm 2 / N, the measured value of the photoelastic coefficient of the same optical film is 21×10 -8 cm 2 / N. In the 6FDA-PFMB layer, Δnd was 0.3 n...

Embodiment 2

[0135] The polyimide solution of Example 1 was coated on a 40 μm thick thermoplastic polymer base film (trade name: ZEONOR, manufactured by Nippon Zeon Co. Ltd), followed by 5% uniaxial stretching in the longitudinal direction, while at 150 °C, thereby obtaining a laminated birefringent optical film having an optical anisotropy of nx>ny>nz. When measured, the photoelastic coefficient of the polymer base film was 4 × 10 -8 cm 2 / N, the thickness is 38 μm. The photoelastic coefficient of the 6FDA-PFMB layer is 98×10 -8 cm 2 / N, the thickness is 6.5 μm. Therefore, the birefringent optical film thus produced has a calculated value of Σ(Cn×Wn) of 18×10 -8 cm 2 / N, the measured value of the photoelastic coefficient of the same optical film is 20×10 -8 cm 2 / N. In the 6FDA-PFMB layer, Δnd is 53nm, Rth is 275nm, and Δnxz is 0.042.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
photoelasticityaaaaaaaaaa
photoelasticityaaaaaaaaaa
photoelasticityaaaaaaaaaa
Login to view more

Abstract

The present invention provides a birefringent optical film having a high orientation for easily obtaining a desired retardation value and also a small photoelastic coefficient. The birefringent optical film includes at least two kinds of polymer materials. A total of products of Cn and Wn satisfies a numerical formula (1): Sigma(CnxWn)<=30X10<-8 >cm<2> / N (1) where Cn and Wn denote respectively a photoelastic coefficient and a volume fraction of each polymer material, and at least one of the polymer materials of the film has a photoelastic coefficient value of at least 60x10<-8 >cm<2> / N.

Description

technical field [0001] The present invention relates to a birefringent optical film, an elliptically polarizing plate using the optical film, and a liquid crystal display using the elliptically polarizing plate with the birefringent film. Background technique [0002] Generally, birefringent films for optical compensation are prepared by film stretching technology, and such birefringent films are used in various liquid crystal displays. For stretching, for example, JP3(1991)-33719A discloses roll tension stretching, roll pressure stretching, and tenter uniaxial stretching. JP3(1991)-24502A discloses that biaxial stretching is performed under anisotropic producing conditions. Regarding other methods of producing birefringent films, for example, JP8(1996)-511812A discloses a method of processing soluble polyimide into a film to obtain negative uniaxiality. [0003] By adopting the above or other techniques for stretching the film, the film can be given optical properties suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/13363G02F1/1335B32B27/08G02B5/30
CPCG02B5/3083B32B27/08C09K2323/00Y10T428/24942Y10T428/31507G02F1/1335
Inventor 西小路祐一村上奈穗林政毅吉见裕之
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap