Composition expressing 10PB 4/1 pigment and technical method for preparing color characterization objects by using the same
A technology of composition and characterization, applied in the direction of pigment paste, color measurement device, device for coating liquid on the surface, etc., can solve the problems of inaccurate control, etc., achieve small color difference, good ratio reproducibility, and weather resistance High performance and stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1:
[0022] Weigh 3.24 grams of PBK7, 27.69 grams of PW6, and 1000 grams of CSC-B base material by weight. Mix the above materials uniformly, and then apply the resulting composition to the substrate evenly and evenly under the conditions of 50%±5% of ambient relative humidity and 23±2°C of room temperature by mechanical coating method. It is a metallic material or a non-metallic material, the wet film thickness of the coating is 250m, and then it is placed in a precision oven at 50±2℃ to dry for 3 to 4 hours to constant weight, taken out, and cooled to room temperature to obtain a color characterization object.
Example Embodiment
[0023] Example 2:
[0024] Weigh 3.2 grams of PBK7, 27.69 grams of PW6, and 1000 grams of CSC-C base material by weight. The production process is the same as in Example 1.
Example Embodiment
[0025] Example 3:
[0026] Weigh 3.24 grams of PBK7, 27.4 grams of PW6, and 1005 grams of CSC-C base material by weight. The production process is the same as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap