Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ammonia-smoking method and flame-proof treatment method for pure cotton knitted fabric

A technology for flame retardant finishing, cotton knitted fabrics, applied in the direction of fabric surface trimming, heating/cooling fabrics, textile material processing, etc., can solve problems such as unsuitability of pure cotton fabrics

Inactive Publication Date: 2010-07-14
江苏华瑞时尚集团有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is generally believed that pure cotton fabrics are not suitable for flame-retardant finishing by the Proban method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ammonia-smoking method and flame-proof treatment method for pure cotton knitted fabric
  • Ammonia-smoking method and flame-proof treatment method for pure cotton knitted fabric
  • Ammonia-smoking method and flame-proof treatment method for pure cotton knitted fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The flame retardant finishing method of pure cotton knitted fabric is as follows. First, the pure cotton knitted fabric is pad-rolled with a flame-retardant finishing solution containing a flame retardant through a sizing machine, and then the pure cotton knitted fabric is pre-dried at 100-120 ° C; Ammonia fumigated cross-linking room, so that the ammonia gas and the flame retardant on the knitted fabric are fully and evenly cross-linked; then oxidized, washed and dried. The flame-retardant effect of the pure cotton knitted fabric obtained through the flame-retardant finishing process of the present invention is uniform in the front, back, left, and right sides, and has no color flower problem.

[0017] see figure 1 , the upper and front parts of the ammonia fumigated crosslinking chamber 13 are provided with a steam inlet 4, the front part is also provided with a hatch 5 for entering the ammonia fumigated crosslinking chamber, and the rear part is provided with an amm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an ammonia-smoking method and a flame-proof treatment method for pure cotton knitted fabric. The flame-proof treatment method comprises the following steps: padding the pure cotton knitted fabric into a flame-proof treatment solution with a fire retardant by a setting machine, and performing pre-drying on the pure cotton knitted fabric at the temperature of 100-120 DEG C; leading the pure cotton knitted fabric to be in a natural suspension state to pass through an ammonia-smoking crosslinking chamber fully filled with ammonia, so that the ammonia can be fully crosslinked with the fire retardant on the knitted fabric evenly; and then performing oxidizing, washing and parching. In the invention, the pure cotton knitted fabric is in a natural loose suspension state to pass through the ammonia-smoking crosslinking chamber, thus the strain suffered by the pure cotton knitted fabric is small and can not cause the deformation and turned edges of the knitted fabric, the anti-flaming effects of the two sides of the shell fabric and the middle part of knitted fabric are the same, and the defect of colored spots can not appear.

Description

technical field [0001] The invention relates to a flame-retardant finishing process for pure cotton knitted fabrics, in particular to an ammonia fumigation method in the flame-retardant finishing process. Background technique [0002] PROBAN is a durable post-treatment flame retardant for cellulose fibers and their blended fabrics. Its main chemical component is tetrakishydroxymethylphosphorus chloride (THPC). The process of using PROBAN for flame-retardant finishing of fabrics is: [0003] Padding flame retardant finishing solution (room temperature)→pre-drying (100~120℃)→ammonia fumigation→oxidation, washing→drying (130~140℃). [0004] The flame retardant finishing method is also called the Proban method, which originated from the British Aowei Company. Specifically, the Proban method is to firstly pad the pure cotton knitted fabric with a flame retardant finishing solution containing a flame retardant through a sizing machine, and then pre-dry the pure cotton knitted fa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B3/16D06B3/18D06B23/04D06C7/00D06M11/60D06M101/06
Inventor 孙广龙张静王敢彭文浩
Owner 江苏华瑞时尚集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com