Manufacturing method of high-strength automobile aluminum-alloy rim material

A manufacturing method and technology of aluminum alloy, which is applied in the field of manufacturing auto parts materials, can solve problems such as poor mechanical properties and limited application range, and achieve the effects of increasing tensile strength, improving mechanical properties, and increasing alloy strength

Inactive Publication Date: 2010-07-21
卢森锴
View PDF3 Cites 58 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a manufacturing method of high-strength automotive aluminum alloy rim material to solve the shortcomings of existing aluminum alloy rims, such as poor mechanical properties and limited application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of high-strength automobile aluminum-alloy rim material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A method for manufacturing a high-strength automotive aluminum alloy rim material, the method comprising the following main steps:

[0056] A. Preparation:

[0057] Prepare the following alloy raw materials by weight percentage:

[0058] Si 0.4%, Mg 0.8%, Ti 0.15%, Zn 0.2%, Fe 0.6%, Cu 0.15%, Cr 0.08%, Mn 0.1%, and Al-Ti-C refiner 0.33%, Al-10% RE master alloy , Al-Zr10% master alloy, Al-10% Sr master alloy and the balance of Al;

[0059] Wherein the weight percentages of Al-10%RE master alloy, Al-Zr10% master alloy and Al-10%Sr master alloy are 0.02% of the total weight of all alloy raw materials according to RE, 0.02% of Zr total weight of all alloy raw materials, Sr accounts for 0.02% of the total weight of all alloy raw materials;

[0060] B. Melting:

[0061] Put the above-mentioned alloy raw materials Si0.4%, Mg 0.8%, Ti0.15%, Zn 0.2%, Fe 0.6%, Cu 0.15%, Cr 0.08%, Mn 0.1% and the rest of Al into the melting furnace, heating the melting furnace, so that All al...

Embodiment 2

[0081] A method for manufacturing a high-strength automotive aluminum alloy rim material, the method comprising the following main steps:

[0082] A. Preparation:

[0083] Prepare the following alloy raw materials by weight percentage:

[0084] Si 0.6%, Mg 1.0%, Ti 0.12%, Zn 0.25%, Fe 0.7%, Cu 0.28%, Cr 0.25%, Mn 0.15%, and Al-Ti-C refiner 1.0%, Al-10% RE master alloy , Al-Zr10% master alloy, Al-10% Sr master alloy and the balance of Al;

[0085] Wherein the weight percentages of Al-10%RE master alloy, Al-Zr10% master alloy and Al-10%Sr master alloy are 0.04% of the total weight of all alloy raw materials according to RE, 0.04% of the total weight of all alloy raw materials by Zr, 0.04% of the total weight of all alloy raw materials, Sr accounts for 0.04% of the total weight of all alloy raw materials;

[0086] B. Melting:

[0087] Put the above-mentioned alloy raw materials Si0.6%, Mg 1.0%, Ti0.12%, Zn 0.25%, Fe 0.7%, Cu 0.28%, Cr 0.25%, Mn 0.15% and the rest of Al into t...

Embodiment 3

[0107] A method for manufacturing a high-strength automotive aluminum alloy rim material, the method comprising the following main steps:

[0108] A. Preparation:

[0109] Prepare alloy raw materials by weight percentage: Si0.8%, Mg1.2%, Ti0.1%, Zn 0.3%, Fe 0.8%, Cu0.4%, Cr 0.32%, Mn 0.2% and Al-Ti-C refinement Agent 2%, Al-10% RE master alloy, Al-Zr10% master alloy, Al-10% Sr master alloy and the balance of Al;

[0110] Wherein the weight percentages of Al-10%RE master alloy, Al-Zr10% master alloy and Al-10%Sr master alloy are 0.06% of the total weight of all alloy raw materials, Zr 0.06% of all alloy raw materials, and 0.06% of all alloy raw materials. Sr accounts for 0.06% of the total weight of all alloy raw materials;

[0111] B. Melting:

[0112] Put the alloy raw materials Si0.8%, Mg 1.2%, Ti0.1%, Zn 0.3%, Fe0.8%, Cu0.4%, Cr0.32%, Mn0.2% and the rest of Al into the furnace, heat Furnace, so that all the alloy raw materials in the furnace are melted into alloy soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method of a high-strength automobile aluminum-alloy rim material, which relates to a manufacturing method of automobile fitting materials. The manufacturing method comprises the following steps of: preparing materials; smelting; adding a refiner; adjusting components; refining; casting; quenching; carrying out aging treatment; and packaging to prepare the high-strength automobile aluminum-alloy rim material which comprises 0.4-0.8 percent of Si, 0.8-1.2 percent of Mg, 0.16-0.22 percent of Ti, 0.2-0.3 percent of Zn, 0.6-0.8 percent of Fe, 0.15-0.4 percent of Cu, 0.08-0.32 percent of Cr, 0.1-0.2 percent of Mn, 0.02-0.06 percent of RE rare earth, 0.02-0.06 percent of Zr, 0.02-0.06 percent of Sr and the balance of Al. The invention has reasonable process parameter and simple manufacturing method, and the manufactured aluminum-alloy rim material has the advantages of high strength, good mechanical performance and the like and is suitable for being popularized and used in small, medium and large automobiles.

Description

【Technical field】: [0001] The invention relates to a method for manufacturing auto parts materials, in particular to a method for manufacturing high-strength aluminum alloy wheel rim materials for automobiles. 【Background technique】: [0002] The rim is the part that fixes and installs the tire in the wheel. It belongs to the automobile security parts. The rim structure has two-piece, three-piece, four-piece, five-piece, etc., and the most commonly used ones are two-piece and three-piece. Rims can be divided into steel rims and aluminum alloy rims according to their manufacturing materials. At present, steel rims are commonly used at home and abroad. These steel rims are manufactured by section steel processing or plate rolling. The material grades are 12LW-GB11262-89, BG380CL, etc., among which the tensile strength of the 12LW-GB11262-89 material is σ b It is 355~470MPa, elongation>30%. Compared with steel rims, aluminum alloy rims have absolute advantages in terms of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03C22C21/08C22F1/047
Inventor 卢森锴韦文儒韦汉龙苏建欢廖树德
Owner 卢森锴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap