Rare earth rubber vulcanization accelerator, and preparation method and application thereof

A technology of rubber vulcanization and accelerator, which is applied in the direction of organic chemistry, can solve the problems of application limitations, and achieve the effects of promoting reinforcement, using safety, and improving mechanical properties

Active Publication Date: 2013-07-17
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned zinc and rare earth dithiocarbamate accelerators are derivatives of secondary amines, which will be oxidized by oxygen in the air during high-temperature vulcanization to generate carcinogenic nitrite, so their application is restricted. Strict restrictions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth rubber vulcanization accelerator, and preparation method and application thereof
  • Rare earth rubber vulcanization accelerator, and preparation method and application thereof
  • Rare earth rubber vulcanization accelerator, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Method for preparing accelerator:

[0037] Dissolve 29.426g (0.2mol) of glutamic acid with 60ml of water, then dropwise add 13.44ml (0.22mol) of carbon disulfide, add dropwise while stirring at a speed of 8 seconds / drop, until the dropwise addition is complete, continue to stir for half Hour. Transfer to a four-necked flask equipped with a cooling device and a thermometer, and raise the temperature to 35° C. for 3 hours in a water bath for reaction. Dissolve 70.08g LaCl in 100ml water 3 ·6H 2 O (0.2mol), after the lanthanum chloride was completely dissolved, was added to the above reaction solution to obtain a white precipitate. Filter, wash, and dry under vacuum at 40°C. The dried product was ground to obtain a off-white powder, namely the target product lanthanum glutamate dithiocarbamate.

[0038] The elemental analysis results are as follows: C: 18.29% (18.36%); H: 2.78% (3.03%); N: 3.56% (3.97%), and the experimental values ​​in brackets indicate that the mole...

Embodiment 2

[0040] Method for preparing accelerator:

[0041] Dissolve 29.426g (0.2mol) of glutamic acid in 60ml of water, then add 13.44ml (0.22mol) of carbon disulfide dropwise at a rate of 6 seconds / drop, and continue stirring for 1 hour after the addition is complete. Transfer to a four-neck flask equipped with a cooling device and a thermometer, and raise the temperature to 45°C for 2 hours in a water bath. Dissolve 70.08g LaCl in 100ml water 3 ·6H 2 O (0.2mol), after the lanthanum chloride was completely dissolved, was added to the above reaction solution to obtain a white precipitate. Filter, wash, and dry under vacuum at 40°C. The dry product is ground to obtain an off-white powder, which is the target product lanthanum glutamate dithiocarbamate.

Embodiment 3

[0043] Method for preparing accelerator:

[0044] Dissolve 29.426g (0.2mol) of glutamic acid in 60ml of water, then add 13.44ml (0.22mol) of carbon disulfide dropwise at a rate of 5 seconds / drop, and continue stirring for half an hour after the addition is complete. Transfer to a four-neck flask equipped with a cooling device and a thermometer, and raise the temperature to 70° C. for 2 hours in a water bath. Dissolve 72.97g SmCl in 100ml water 3 ·6H 2O (0.2mol), until the samarium chloride is completely dissolved, is added to the above reaction solution to obtain a white precipitate. Filtrate, wash, vacuum dry and grind at 40°C to obtain a gray-white powder, which is the target product samarium glutamic acid dithiocarbamate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

A rare earth rubber vulcanization accelerator, preparation method and application thereof are provided. The accelerator is composed of rare earth ion and carboxyl substituted dithiocarbamate. The preparation method comprises the following steps: dissolving amino acid in water, dropping CS2, stirring for reaction, adding rare earth compound to obtain precipitate, then filtering, washing and drying. There is no need to add other vulcanization activator (such as stearic acid and zinc oxide) when the accelerator is used to vulcanize rubber and the prepared rubber composite has excellent integrated mechanical property. Furthermore, the accelerator is a primary amine compound, and is environmentally friendly without nitrite generated during the vulcanization.

Description

technical field [0001] The present invention relates to a rare earth rubber vulcanization accelerator and its preparation method and application. This accelerator can well promote the vulcanization of rubber, and also has the functions of surface modification of fillers, improvement of filler dispersion in polymers and Improve the functions of the interface between the filler and the rubber matrix, thereby improving the comprehensive physical and mechanical properties of the vulcanized rubber. Background technique [0002] Vulcanization accelerator is a main rubber additive. The use of vulcanization accelerators can reduce the vulcanization temperature, shorten the vulcanization time, reduce the amount of sulfur, increase the vulcanization rate, reduce the cost of the product, improve the physical and mechanical properties of the product, and have important practical significance for energy saving and consumption reduction and improving the performance of rubber products. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L21/00C08L9/06C08K5/39C08J3/24C07C333/16
CPCC08J2309/06C08K5/39C08J2321/00C07C333/16C08F236/10C08J3/24C08F4/44
Inventor 罗远芳刘岚杨树颜
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap