An azo dye and mixture technology, applied in the field of disperse black azo dye mixture and its preparation, can solve the problems of dye depth, insufficient lifting force, poor levelness, poor fastness, etc., and achieve excellent sublimation fastness, good Good affinity and dyeing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0066] Example 1
[0067] Add 15.1 g of dye of formula (Ib), 13.2 g of dye of formula (IIa), 14.8 g of dye of formula (IIIa), 6.9 g of dye of formula (Va), 50 g of sodium lignosulfonate, and 300 ml of water After mixing, use a grinder to grind and disperse, and spray dry (inlet temperature is 130°C, outlet temperature is 60°C) to obtain 100 grams of finished product. 0.4g of this product was dyed for 10g of polyester fiber at pH 4.5 and 130°C for 60 minutes, and then washed, rinsed, and dried to obtain bright black dyed products with excellent fastness properties.
[0068]
Example Embodiment
[0069] Example 2
[0070] Add 11.2 g of dye of formula (Ib), 11.3 g of dye of formula (IIa), 13.5 g of dye of formula (IIIa), 6 g of dye of formula (Va), 98 g of sodium lignosulfonate, and add 450 ml of water After mixing, the dye mixture was prepared according to the method of Example 1, and then 10 grams of polyester fiber was dyed according to the method of Example 1, to obtain bright black dyed products with excellent fastness properties.
Example Embodiment
[0071] Example 3
[0072] After mixing 5.2 g of the dye of formula (Ia), 9.8 g of the dye of formula (IIb), and 10 g of sodium lignosulfonate, adding 75 ml of water, the mixture was ground and dispersed with a grinder to obtain an aqueous dye product. One gram of the product was dyed with 10 grams of polyester fiber according to the method of Example 1, to obtain a bright navy blue dyed product with excellent washing and various fastness properties.
[0073]
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap