smooth clay drawing board

A clay and drawing board technology, used in the field of art painting tools, can solve the problems of yellowing, brittleness, cracking and other problems of the material, and achieve the effect of changing the unevenness, improving the flatness and enhancing the contrast.

Active Publication Date: 2015-11-11
WUXI PHOENIX ARTIST MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ordinary gypsum drawing boards will turn yellow, become brittle, and crack after being left for a long time, which will affect the preservation and collection of art works. Clay coating can completely solve the above problems, and has anti-oxidation properties, so that the coating will not crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The smooth clay drawing board preparation procedure of the present embodiment is as follows:

[0018] (1) Add 200 parts of deionized water, 2 parts of defoamer, 20 parts of propylene glycol, and 5 parts of dispersant into the reaction kettle, stir evenly, and the stirring speed is 1800 rpm;

[0019] (2) Add 150 parts of titanium dioxide, 150 parts of kaolin (ultrafine calcined kaolin produced by Shanxi Jinyang Calcined Kaolin Co., Ltd., model HA-90), 200 parts of talcum powder and disperse for 1 hour, add 350 parts of pure acrylic emulsion and stir evenly, stirring at a speed of 3500 rev / min;

[0020] (3) Add multifunctional additive AMP-95 to adjust the pH value to 7.0, while stirring, add 2 parts of defoamer, 10 parts of film-forming aid, 50 parts of thickener ASE-6050, and 1 part of thickener TT9351, and continue stirring , and the stirring speed is 3000 rpm / min, and the coating can be sprayed;

[0021] (4) Apply the prepared paint to the surface of the poplar boar...

Embodiment 2

[0023] The smooth clay drawing board preparation procedure of the present embodiment is as follows:

[0024] (1) Add 180 parts of deionized water, 2.5 parts of defoamer, 18 parts of propylene glycol, and 5.5 parts of dispersant into the reaction kettle, stir evenly, and the stirring speed is 2000 rpm;

[0025] (2) Add 145 parts of titanium dioxide, 160 parts of kaolin (ultrafine calcined kaolin produced by Shanxi Jinyang Calcined Kaolin Co., Ltd., model HA-90), 220 parts of talcum powder and disperse for 1 hour, add 350 parts of pure acrylic emulsion and stir evenly, stirring at a speed of 3000 rev / min;

[0026] (3) Add multifunctional additive AMP-95 to adjust the pH value to 7.0, and add 1.5 parts of defoamer, 11 parts of film-forming aid, 45 parts of thickener ASE-6045 and 1.2 parts of thickener TT935 while stirring. Continue to stir, and the stirring speed is 3000 rpm / min, and the coating must be sprayed;

[0027] (4) Apply the prepared paint to the surface of the poplar...

Embodiment 3

[0029] The smooth clay drawing board preparation procedure of the present embodiment is as follows:

[0030] (1) Add 220 parts of deionized water, 1.5 parts of defoamer, 22 parts of propylene glycol, and 4.5 parts of dispersant into the reaction kettle, stir evenly, and the stirring speed is 1800 rpm;

[0031] (2) Add 155 parts of titanium dioxide, 140 parts of kaolin (ultrafine calcined kaolin produced by Shanxi Jinyang Calcined Kaolin Co., Ltd., model HA-90), 180 parts of talcum powder and disperse for 1 hour, add 350 parts of pure acrylic emulsion and stir evenly, stirring at a speed of 3800 rev / min;

[0032] (3) Add multifunctional additive AMP-95 to adjust the pH value to 7.0, while stirring, add 2.5 parts of defoamer, 9 parts of film-forming aid, 55 parts of thickener ASE-605, and 1.5 parts of thickener TT935, Continue to stir, and the stirring speed is 3500 rpm / min, and the coating must be sprayed;

[0033] (4) Apply the prepared paint to the surface of the poplar boa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a universal smooth clay drawing board which is prepared through the processes: 180-220 parts of deionized water, 1.5-2.5 parts of defoaming agent, 18-22 parts of propylene glycol and 4.5-5.5 parts of dispersing agent into a reaction kettle, and uniformly stirring all the components; adding 145-155 parts of titanium dioxide, 140-160 parts of kaoline and 180-220 parts of talcum powder, dispersing for 1h, adding 340-360 parts of pure acrylic emulsion, and uniformly stirring; adding a multifunctional assistant AMP-95 to adjust the pH value to 7.0, and adding the 1.5-2.5 parts of defoaming agent, 9-11 parts of film-forming additive, 45-55 parts of thickening agent ASE-60 and 1-1.5 parts of thickening agent TT935 while stirring to obtain a coating for curtain coating; and carrying out curtain coating on a base material to obtain the universal smooth clay drawing board. A clay coating of the drawing board is sunproof, acid-resistant and corrosion-resistant so as to ensure that a work is not cracked or faded after being stored and placed for a long term; the clay coating can be thickened or thinned randomly so as to be beneficial to the perfect presentation of details of the work.

Description

technical field [0001] The invention relates to an art painting utensil, in particular to a smooth clay drawing board suitable for coloring with various pigments. Background technique [0002] Ordinary gypsum drawing boards will turn yellow, become brittle, and crack after being left for a long time, which will affect the preservation and collection of art works. Clay coating can completely solve the above problems, and it has oxidation resistance, so that the coating will not crack. During the Renaissance, this clay coating was used as a special coating for centuries-old murals in churches, making it still colorful and well preserved after thousands of years of light and air oxidation. The coating has a museum quality, but the technique has long been lost. Contents of the invention [0003] In view of the above-mentioned defects existing in the prior art, the purpose of the present invention is to provide a kind of wrinkled surface clay drawing board. The drawing board ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D7/12C09D5/08B05D7/06B05D7/24B44D3/18
Inventor 陈卫宏陈祎
Owner WUXI PHOENIX ARTIST MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com