Polypropylene composition for folding stool and preparation method thereof

A polypropylene composition and a technology for copolymerizing polypropylene are applied in the field of polypropylene compositions for folding stools and their preparation, which can solve the problems of poor scratch resistance, easy freeze cracking, low rigidity, etc. gorgeous effect

Active Publication Date: 2013-07-31
安徽龙和电力集团有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polypropylene is a common general-purpose plastic, which is polymerized from propylene monomers. The English abbreviation is PP. The material has poor heat resistance, a melting point of 165-175°C, low rigidity, low impact toughness, relatively low hardness, and poor low temperature resistance. , poor scratch resistance, in the field of modified plastics, it is difficult to improve its rigidity and toughness, scratch resistance and low temperature resistance at the same time, so it cannot be directly used as raw materials for folding stools
According to the polymerization method, the arrangement of molecular segments of polypropylene is mainly divided into two categories: copolymerized polypropylene and homopolypropylene. Among them, homopolypropylene has poor toughness and high rigidity, and the notched impact strength is 3.0-5.0KJ / m 2 , flexural modulus 1400-2200Mpa; copolymerized polypropylene has high impact toughness, but low rigidity, notched impact strength 5.0-50.0kg / m 2 , the flexural modulus is 700-1500mpa, and the Brinell hardness of the copolymerized polypropylene PP is as low as 30-60, and it is easy to freeze and crack outdoors in severe cold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The folding stool polypropylene composition of the present embodiment, its raw material formula is to be made up of each component of following parts by weight:

[0045] 50 parts of copolymerized polypropylene;

[0046] 35 parts of recycled polypropylene copolymer;

[0047] Calcium carbonate 12 parts;

[0048] 5 parts of polyolefin elastomer;

[0049] Antioxidant 1010 0.2 parts;

[0050] Antioxidant 168 0.3 part;

[0051] Anti-ultraviolet agent UV-531 0.3 parts;

[0052] Diffusion powder EBS 0.08 parts;

[0053] 3130 Everlasting Red F2R 0.02 parts.

[0054] The preparation method of the polypropylene composition for the above-mentioned folding stool specifically comprises the following steps:

[0055] According to the dosage of the formula, mix polypropylene copolymer, polypropylene recycled material, calcium carbonate, polyolefin elastomer, antioxidant 1010, antioxidant 168, anti-ultraviolet agent UV-531, diffusing powder EBS and 3130 Everlasting Red F2R evenly A...

Embodiment 2

[0066] The folding stool polypropylene composition of the present embodiment, its raw material formula is to be made up of each component of following parts by weight:

[0067] 30 parts of polypropylene copolymer;

[0068] 50 parts of recycled polypropylene copolymer;

[0069] 16.2 parts of calcium carbonate;

[0070] 5 parts of polyolefin elastomer;

[0071] Antioxidant 1010 0.2 parts;

[0072] Antioxidant 168 0.3 part;

[0073] Anti-ultraviolet agent UV-531 0.3 parts;

[0074] Diffusion powder EBS 0.08 parts;

[0075] 3130 Yonggu Dahong F2R 0.02 copies;

[0076] 0.02 parts of 204 yellow;

[0077] The above-mentioned 204 yellow is the commercially available Taiwan Dagong pigment 204 yellow.

[0078] The preparation method of the polypropylene composition for the above-mentioned folding stool specifically comprises the following steps:

[0079] According to the dosage of the formula, the copolymerized polypropylene, recycled polypropylene copolymer, calcium carbonate,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
impact strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene composition for folding stool and a preparation method thereof. The material formula of the polypropylene composition for folding stool is composed of 30-50 parts of co-polypropylene, 30-50 parts of co-polypropylene reworked material, 10-30 parts of calcium carbonate, 5-10 parts of toughener, 0.1-0.5 parts of antioxidant 1010, 0.1-0.5 parts of antioxidant 168, 0.3-0.5 parts of anti-ultraviolet ray agent UV-531, 0.08-0.1 parts of diffusing powder EBS, 0-0.04 parts of 3130 everlasting red F2R, 0-0.02 parts of everlasting purple RXS, 0-0.02 parts of ritanium of dracocephalum moldavica, and 0-0.02 parts of 204 yellow according to weight parts. The polypropylene composition for folding stool of the invention meets each index of the folding stool; and thefolding stool is widely used in open air, and has the characteristics of beautiful color, sun-proof, water-proof, high rigidity, impact resistance, scuffing resistance, low temperature resistance, high resistance, and aging resistance. In this way, the folding stool can be recycled.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polypropylene composition for folding stools and a preparation method thereof. Background technique [0002] Polypropylene is a common general-purpose plastic, which is polymerized from propylene monomers. The English abbreviation is PP. The material has poor heat resistance, a melting point of 165-175°C, low rigidity, low impact toughness, relatively low hardness, and poor low temperature resistance. , Poor scratch resistance. In the field of modified plastics, it is difficult to improve both rigidity and toughness, scratch resistance, and low temperature resistance at the same time, and cannot be directly used as raw materials for folding stools. According to the polymerization method, the arrangement of molecular segments of polypropylene is mainly divided into two categories: copolymerized polypropylene and homopolypropylene. Among them, homopolypropylene has poor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L23/08C08L47/00C08L9/06C08L23/20C08K13/02C08K3/26B29B9/06B29C47/92B29C48/92
CPCB29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 杜崇铭林湖彬
Owner 安徽龙和电力集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com