Magnetic cool storage material

A cold storage material and magnetic technology, applied in the field of magnetic cold storage materials, can solve the problems of reducing the specific heat of lead and reducing the efficiency of the cold accumulator, and achieve the effect of high specific heat peak value and wide coverage temperature range.

Active Publication Date: 2014-05-07
UNIV OF SCI & TECH BEIJING
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the low temperature region below 15K, the specific heat of lead decreases sharply with the decrease of temperature, so that the efficiency of the cold storage is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetic cool storage material
  • Magnetic cool storage material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Prepare HoCu according to the prescribed stoichiometric ratio 1.9 Ni 0.1 , the ingot is prepared by melting in an intermediate frequency induction heating furnace, and then processed into spherical particles by centrifugal atomization equipment.

Embodiment 2

[0025] Prepare HoCu according to the prescribed stoichiometric ratio 1.7 Ni 0.3 , the ingot was prepared by melting in an intermediate frequency induction heating furnace, and then spherical particles were prepared by a rotating electrode method.

Embodiment 3

[0027] Prepare HoCu according to the prescribed stoichiometric ratio 1.5 Ni 0.5 , the medium frequency induction heating furnace is used to prepare ingots, which are directly mechanically crushed into particles, and the particles with a size of 0.154~0.3mm are screened, which can be directly used as regenerator fillers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a HoCu[2-x]Nix series magnetic cool storage material for a cryo refrigerator. The magnetic cool storage material has larger volumetric specific heat in 10-40K temperature area, has larger width of specific heat peak, and can substitute for Pb to be used as the cool storage material for 10-40K temperature area. The HoCu[2-x]Nix series magnetic cool storage material has the outstanding characteristics that the position and the specific heat peak value can be regulated by controlling the content of Ni, when the additive proportion x of Ni is equal to 0.4, the material has specific heat peak at 20.2K, and the specific heat peak value is 0.95J / cm<3>K. According to the HoCu[2-x]Nix series magnetic cool storage material, the cast ingot can be directly manufactured into particle materials for use by a mechanical crushing method, or can be manufactured into spherical particle materials for use by a melt atomization method or a rotation electrode method, and 0.154-0.30mm spherical particle is in the best use form.

Description

technical field [0001] The invention relates to a magnetic cold storage material for a cryogenic refrigerator. The specific heat characteristic of the series of magnetic cold storage materials can be adjusted in a temperature range of 10K to 40K, and can be used as a cold storage material instead of metal Pb. Background technique [0002] With the rapid development of science and technology, the demand for various small and high-efficiency low-temperature refrigerators is increasing day by day. Among them, the small cold-storage gas refrigerator using helium as the working medium has been widely used in various cutting-edge technical fields due to its reliable performance and simple structure. For small cold-storage gas refrigerators, the cold storage is the key component. The performance of cold storage materials has a direct impact on the performance of the refrigerator, which ultimately determines the cooling efficiency and the lowest possible cooling temperature. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/06B22F9/10B22F9/04
Inventor 叶荣昌贾远航龙毅
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com