Preparation method of fine-denier high-shrinkage composite filament plain weave fabric

A high-shrinkage, composite yarn technology, applied in the processing of textile materials, continuous processing of textile materials, dyeing methods, etc., can solve problems such as uneven fabrics, poor color fastness, and premature shrinkage

Active Publication Date: 2015-12-23
SUZHOU RUIZHONG NEW MATERIAL TECH CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The warp and weft yarns of the fine-denier high-shrinkage composite yarn plain fabric use high-shrinkage cotton-like fibers, and the high-shrinkage cotton-like fibers are composite yarns made of polyester high-shrinkage yarns and polyester porous yarns. It is easy to shrink prematurely in the state, therefore, the fabrics produced by the preparation method in the prior art often have unevenness
The problem of poor color fastness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of fine-denier high-shrinkage composite filament plain weave fabric
  • Preparation method of fine-denier high-shrinkage composite filament plain weave fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The invention discloses a method for preparing a fine denier high shrinkage composite silk plain weave fabric. The fine denier high shrinkage composite silk plain weave fabric is prepared from raw materials through warping, sizing, weaving, washing with alkali, dyeing, washing, color fixing and shaping.

[0021] Raw material: The raw material is 80D / 156F high-shrinkage cotton-like fiber, purchased from Taicang Jinhui Chemical Fiber Industry Co., Ltd.

[0022] Warping: use Tsudakoma KSH500 pulping and equipment for warping and sizing, and use Tsudakoma KSH500 pulping and equipment hydrostatic pressure device for section warping.

[0023] Sizing: Water-soluble polyester size with a mass concentration of 12% is used for sizing, and the sizing speed of Tsudakoma KSH500 type sizing equipment is controlled to 220m / min, the rear oiling roller is 10r / min, and the silk output tension is 11kg, coiling tension is 15kg, draft A=0%, draft B=+1.1%, size tank temperature is 50°C, dryi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of fine-denier high-shrinkage composite filament plain weave fabric. The fine-denier high-shrinkage composite filament plain weave fabric is prepared from raw materials through warping, sizing, plain weave weaving, washing alkali metering, dyeing, washing, fixation and shaping. The raw materials are high-shrinkage cotton-imitated fibers. The specific method of dyeing includes the steps that a gray fabric obtained after washing alkali metering is placed in dyeing fluid, uniform dyeing is conducted for 5-15 min after temperature rises to 50-60 DEG C, uniform dyeing is conducted for 5-15 min after temperature rises to 70-80 DEG C, then after heat is preserved for 30-60 min after temperature rises to 125-130 DEG C, the dyeing fluid is drained at the temperature of 75-85 DEG C, reduction cleaning is conducted for 20-30 min through reaction cleaning fluid at the temperature of 80-90 DEG C, and then dyeing is finished. The preparation method is improved, and the fabric has the advantages of achieving cotton velvet feeling and being soft in gloss, fluffy, breathable, elegant, fashionable and the like, and meets the requirements for wear individuality, health and comfort.

Description

technical field [0001] The invention relates to a preparation method of a fine-denier high-shrinkage composite silk plain weave fabric. Background technique [0002] The warp and weft yarns of the fine-denier high-shrinkage composite yarn plain fabric use high-shrinkage cotton-like fibers, and the high-shrinkage cotton-like fibers are composite yarns made of polyester high-shrinkage yarns and polyester porous yarns. It is easy to shrink prematurely in the state, therefore, the fabric produced by the preparation method in the prior art often has unevenness. The problem of poor color fastness. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing a fine-denier high-shrinkage composite silk plain weave fabric, which has the characteristics of velvet feeling, soft luster, fluffy and breathable. [0004] In order to solve the above technical problems, the present invention takes the following techni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D06B21/00D06P1/16D06P1/653D06P3/60D06L1/16
Inventor 黄志向曹茂松翟涛曹国兰钮彦艳
Owner SUZHOU RUIZHONG NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap