A kind of iron-zinc coated steel plate with a yield strength of 210mpa and its production method

A yield strength, 210mpa technology, applied in the field of iron-zinc coated steel plate and production, can solve the problems of high maintenance cost, complex equipment, high investment, and achieve the effect of dense surface structure, firm bonding, and not easy to powder and fall off

Active Publication Date: 2018-05-01
武汉钢铁有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If a fully enclosed alloying furnace is used, the one-step heating method can be used, but the investment of this equipment is high, the equipment is complicated, and the cost of maintenance and accessories is also high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of iron-zinc coated steel plate with a yield strength of 210mpa and its production method
  • A kind of iron-zinc coated steel plate with a yield strength of 210mpa and its production method
  • A kind of iron-zinc coated steel plate with a yield strength of 210mpa and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The present invention is described in detail below:

[0027] Table 1 is the value list of the chemical components of each embodiment of the present invention and comparative examples;

[0028] Table 2 is the value list of the main process parameters of each embodiment of the present invention and comparative examples;

[0029] Table 3 is a list of tensile properties and coating quality of each embodiment of the present invention and comparative examples.

[0030] Each embodiment of the present invention is all produced by following process:

[0031] 1) Carry out continuous hot-dip galvanizing on the cold-rolled steel plate, and control the temperature of the zinc pot at 455~465°C, and control the temperature of the strip steel into the zinc pot at 460~490°C; control the aluminum weight percentage content in the zinc solution at 0.08- 0.12%;

[0032] 2) After galvanizing, the steel plate is sent to the zinc-iron diffusion treatment heating furnace under the heat prese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

An iron-zinc coated steel plate with the yield strength being 210 MPa comprises chemical compositions including, by weight, 0.03-0.04% of C, 0.007-0.015% of Si, 0.32-0.4% of Mn, less than or equal to 0.02% of P, less than or equal to 0.01% of S, 0.015-0.05% of Als and less than or equal to 0.05% of N. The production method comprises the production steps that continuous hot-dip galvanizing is conducted on a cold-rolled steel plate; the steel plate is sent to an iron-zinc diffusion treatment heating furnace by taking insulation measures; the galvanized steel plate is subjected to high-temperature zinc-iron diffusion treatment first and then low-temperature zinc-iron diffusion treatment; and the steel plate is cooled naturally to the roor temperature for standby application. By means of the production method, on the premise of guaranteeing the application mechanics of the steel plate, a galvanneal coating can be compact in surface structure and free of obvious microcrack defects, and zinc-iron grains on the surface of the coating are fine and uniform in size distribution. The coating is bound firmly to a steel base plate. The coating is not prone to pulverization and shedding during stamping forming.

Description

technical field [0001] The invention relates to a galvanized steel plate and a production method thereof, in particular to an iron-zinc coated steel plate with a yield strength of 210 MPa and a production method thereof, and is suitable for a steel plate with a thickness of 0.7-1.2 mm. Background technique [0002] Zinc-iron coated steel sheet (GA) has excellent corrosion resistance, paintability, weldability and anti-gravel performance, and is widely used in automobile panels. However, zinc slag and zinc ash are prone to appear on the surface of the coating, and the iron content and phase structure of the coating cross-section are unevenly distributed. Defects such as shedding and pulverization of the coating are prone to occur during stamping and forming, which will affect the surface quality of stamping parts and production molds. Negative Effects. [0003] After patent search, a production method of non-powdering thick-gauge zinc-iron alloyed plate was found. The strip ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C23C2/06C23C2/28C23C10/28
CPCC22C38/02C22C38/04C22C38/06C23C2/06C23C2/28C23C10/28
Inventor 陈宇杜晓峰彭涛方芳胡宽辉潘利波李立军张彦文王立辉
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products