Black glaze cup adobe vintage formula and preparation method

A black glaze and formula technology, applied in clay products, applications, household appliances, etc., can solve the problems of low brightness of glaze, insufficient blackness of cultured products, weak artistic appeal, etc., and achieve strong artistic appeal. , the effect of sufficient blackness

Inactive Publication Date: 2018-08-14
福建省东丰阁文化发展有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing ancient formula and preparation method of black-glazed calyx clay cannot ensure the content of Fe2o3, and the fired products cannot achieve sufficient blackness, and the glaz

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black glaze cup adobe vintage formula and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0022] See figure 1 , The present invention provides a technical solution: a black-glazed calyx embryo soil retro formula, raw materials: feldspar, quartz, red stone, soil, iron red powder, red soil as the embryo, the ratio is 5:3:2: 2:5:5, with plant ash and iron ore as glaze:

[0023] The chemical composition of the dry matter of the black glaze cup is: Fe2o34-8%, CaO6--9%, MgO2--5%, Al2O315-20%, P2O52-4%;

[0024] A method for preparing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a black glaze cup adobe vintage formula and a preparation method. The black glaze cup adobe vintage formula comprises the following raw materials of blank, plant ash and iron ore, wherein the blank is prepared from 5 parts of feldspar, 3 parts of quartz, 2 parts of akaishi, 2 parts of herba szechwan podocarpii, 5 parts of iron red powder and 5 parts of red soil, the plant ash burnt by plants and the iron ore are taken as glaze; the chemical ingredients of black glaze cup dry substances is 4-8% of Fe2O3, 6-9% of CaO, 2-5% of MgO, 15-20% of Al2O3 and 2-4% of P2O5. The preparation method comprises the following steps: S1: making earth; S2: making glaze; S3: applying the glaze for the first time; S4: drying for the first time; S5: applying the glaze for the second time;S6: carrying out drying and forming for the second time. In S1, 5 parts of feldspar, 3 parts of quartz, 2 parts of akaishi, 2 parts of herba szechwan podocarpii, 5 parts of iron red powder and 5 parts of red soil are selected and mixed, a proper quantity of water is added, a simple ball mill is adopted for grinding, grinding time is 48 hours, and then, the ground mixed materials are sieved. In the black glaze cup adobe compound formula, the contents of Fe2O3 are ensured, and a burnt sintering product can achieve enough blackness.

Description

Technical field [0001] The invention relates to the technical field of black-glazed cups, in particular to a black-glazed cups embryonic retro formula and preparation method. Background technique [0002] The black glaze cup is one of the most typical tea sets in the Song Dynasty. It was produced in large quantities for the needs of ordering tea and fighting tea. Song people fighting tea must use the precious "Jian Gao". According to Cai Xiang’s “Tea Records” in the first record: “It was created by Jian’an, the wrong black, if the pattern is free of it, it is still slightly thick, dry for a long time, hot and cold, the most useful.” The black base of the Song Dynasty is used to build secrets. As a representative, one of the main reasons is that the Yecha Garden in the Song Dynasty is located in the Fenghuangshan area of ​​Jian'ou, Fujian. The electricity production of Longfeng Tuanbing Tea further stimulated the development of Jianmi porcelain. [0003] However, the existing black...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/132C03C8/00C04B33/34C04B41/86
CPCC03C8/00C04B33/1322C04B33/34C04B41/009C04B41/5022C04B41/86C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3272C04B2235/3418C04B2235/3463Y02P40/60
Inventor 周辉黄建
Owner 福建省东丰阁文化发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap