Stripping solution and stripping process for stripping glass ncvm film
A technology for stripping solution and glass, applied in the field of stripping solution and stripping process, can solve problems affecting product appearance quality, unstable product yield, photosensitive ink damage, etc., to achieve good appearance, good stripping effect, guarantee gloss effect
Active Publication Date: 2021-12-14
LENS TECH CHANGSHA
View PDF7 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Traditionally, a strong alkaline stripping solution is used to remove the NCVM film layer, but using this type of stripping solution for stripping is easy to cause damage to the photosensitive ink after exposure and development, affecting the appearance quality of the product, which cannot meet the demand, and The current deplating process has low production efficiency and unstable product yield
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0118] A tandem for retarding the glass NCVM membrane layer consists of the following mass percentage component: 15% sodium carbonate, 10% sodium tartrate, JFC 3%, and the rest is water.
Embodiment 2
[0120] A tandem for retarding the glass NCVM film, consists of a component of the following mass content: 25% sodium carbonate, 5% sodium trihydrate, 1% osmotic JFC, and the rest is water.
Embodiment 3
[0122] A rubber solution for retarding the glass NCVM film, consists of the following mass percentage component: 20% sodium carbonate, 8% sodium tartrate, 2% osmotic JFC, and the rest is water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| density | aaaaa | aaaaa |
| melting point | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a deplating solution and a deplating process for removing glass NCVM film, and relates to the technical field of glass deplating. The deplating solution includes the following components in terms of mass percentage: soluble carbonate 10-30% , complexing agent 5-15%, penetrating agent 1-5%, and the rest is water. The stripping process uses the above-mentioned stripping solution to strip the NCVM film layer of the glass product. The invention alleviates the technical problems that the strong alkaline deplating solution traditionally used for the stripping of the NCVM film easily causes damage to the photosensitive ink after exposure and development, and the product yield is low. The stripping solution of the present invention uses soluble carbonate as the main stripping agent, and by cooperating with complexing agent and penetrant, not only can strip NCVM film cleanly, the stripping effect is good, and it will not affect the exposure and development The final photosensitive ink will cause damage, and the glass products after deplating using this deplating solution have good appearance and high yield.
Description
technical field [0001] The invention relates to the technical field of glass deplating, in particular to a deplating solution and a deplating process for stripping glass NCVM film layers. Background technique [0002] With the progress of society, 2D, 2.5D or 3D glass has been applied to various electronic products and has become a fashion. Compared with traditional plastic and metal mobile phone battery covers, 2D, 2.5D or 3D glass is thinner, transparent and clean , anti-fingerprint, anti-glare, scratch resistance and weather resistance. At present, the deplating process has been well used on glass as a new type of operation method. This process can not only obtain beautiful and precise patterns, but also the patterns have no concave-convex feeling and fine texture. [0003] NCVM (Non-Conductive Vacuum Metalize, vacuum non-conductive electroplating) is a non-conductive vacuum metallization coating process. NCVM uses special metals. This process not only makes the coated f...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C03C23/00
CPCC03C23/0075
Inventor 饶桥兵蔡杰勇
Owner LENS TECH CHANGSHA