Deplating solution, deplating process and glass products obtained by stripping glass ncvm film

A deplating solution and film layer technology, which is applied in the field of glass products, can solve the problems of photosensitive ink, silk screen curing ink damage, poor removal effect of NCVM film layer, unclean removal of NCVM film layer, etc., and achieve good removal effect , The ink layer is well maintained, and the deplating effect is good

Active Publication Date: 2021-09-28
LENS TECH CHANGSHA
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditionally, high-temperature and strong alkaline stripping solution is used to remove the NCVM film layer, but using this type of stripping solution for stripping is easy to cause damage to the photosensitive ink and screen printing cured ink after exposure and development, thus affecting the appearance quality of the product. Satisfy the production demand; while using high-temperature weak alkaline stripping solution or low-temperature strong alkaline stripping solution does not damage the ink, but the stripping effect on the electroplated NCVM film is poor, and the stripping of the NCVM film is not clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] A kind of stripping solution for stripping glass NCVM film layer, described stripping solution comprises pre-stripping solution, main stripping solution and auxiliary stripping solution; Described pre-stripping solution comprises the group of following mass percentage content Composition: hydrogen peroxide 50%, ethylene glycol 10%, carbon secondary alcohol polyoxyethylene ether 1%, sodium bicarbonate 0.1%, and the rest is water;

[0071] The main stripping solution includes the following components in mass percentage: 8% sodium carbonate, 2% EDTA-2Na, 1% sodium α-alkenyl sulfonate, 2% carbon secondary alcohol polyoxyethylene ether, and the rest is water ;

[0072] The auxiliary stripping solution includes the following components in mass percentage: 50% hydrogen peroxide, 10% methanol, 1% lauryl alcohol polyoxyethylene ether, 0.1% sodium carbonate, and the rest is water.

Embodiment 2

[0074] A kind of stripping solution for stripping glass NCVM film layer, described stripping solution comprises pre-stripping solution, main stripping solution and auxiliary stripping solution; Described pre-stripping solution comprises the group of following mass percentage content Composition: hydrogen peroxide 60%, isopropanol 15%, carbon primary alcohol polyoxyethylene ether 3%, potassium bicarbonate 0.5%, and the rest is water;

[0075] The main stripping solution includes the following components in mass percentage: 10% potassium carbonate, 5% EDTA-4Na, 3% sodium secondary alkylsulfonate, 4% isooctyl alcohol polyoxyethylene ether, and the rest is water;

[0076] The auxiliary stripping solution includes the following components in mass percentage: 60% hydrogen peroxide, 15% n-propanol, 3% isooctyl alcohol polyoxyethylene ether, 0.5% potassium carbonate, and the rest is water.

Embodiment 3

[0078] A kind of stripping solution for stripping glass NCVM film layer, described stripping solution comprises pre-stripping solution, main stripping solution and auxiliary stripping solution; Described pre-stripping solution comprises the group of following mass percentage content Parts: hydrogen peroxide 53%, ethanol 12%, branched 10-carbon Guerbet alcohol polyoxyethylene ether 1.6%, potassium carbonate 0.3%, and the rest is water;

[0079] The main stripping solution includes the following components in mass percentage: 8.6% potassium carbonate, 3% EDTA-2Na, 1.6% sulfonate of ethoxylated fatty acid methyl ester, 2.6% JFC, and the rest is water;

[0080] The auxiliary stripping solution includes the following components in mass percentage: 53% hydrogen peroxide, 12% ethanol, 1.6% branched 10-carbon Guerbet alcohol polyoxyethylene ether, 0.3% potassium carbonate, and the rest is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of glass deplating, in particular, it provides a deplating solution for removing a glass NCVM film layer, a deplating process and a glass product obtained by deplating. The described stripping solution that is used to remove glass NCVM film layer comprises pre-stripping solution, main stripping solution and auxiliary stripping solution; The pH of described pre-stripping solution is 7-8, and the pH of described main stripping solution The pH is 10-12, and the pH of the auxiliary stripping solution is 7-8. Using the above-mentioned specific pH pre-deplating solution, main deplating solution and auxiliary deplating solution to perform step-by-step deplating on the glass NCVM film layer, not only can effectively remove the glass NCVM film layer, but also will not damage the surface of the film layer Photosensitive ink or silk screen curing ink, etc., the deplating effect is good, and the product yield after deplating is high.

Description

technical field [0001] The invention relates to the field of glass stripping, in particular to a stripping solution for stripping glass NCVM film layers, a stripping process and a glass product obtained by stripping. Background technique [0002] With the progress of society, 2D, 2.5D or 3D glass has been applied to various electronic products and has become a fashion. Compared with traditional plastic and metal mobile phone battery covers, 2D, 2.5D or 3D glass is thinner, transparent and clean , anti-fingerprint, anti-glare, scratch resistance and weather resistance. Electroplating NCVM (Non-Conductive Vacuum Metalize, vacuum non-conductive electroplating) film on glass has become a fashion and a trend, so the requirements for the deplating process are becoming more and more stringent. [0003] NCVM is applied to glass products of electronic equipment, and a part of the NCVM product is selectively removed after coating, so as to give the coating layer a patterned effect. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C23/00
CPCC03C23/0075
Inventor 周群飞蔡杰勇
Owner LENS TECH CHANGSHA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap