CF/Peek with interlayer shear strength and flexural strength and preparation method thereof

A technology of flexural strength and shear strength, which is applied in the field of CF/PEEK and its preparation between high-rise shear strength and flexural strength, and can solve problems such as difficult to realize industrial production

Active Publication Date: 2021-01-05
DONGHUA UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The CF / PEEK composite material prepared by the above-mentioned known technology usually has an ILSS of less than 85MPa, and the bending strength is usually not more than 700MPa. A few technologies have an ILSS of more than 90MPa and a bending strength of more than 700MPa. However, strong acid or plasma treatment is used in the preparation process. Difficult to achieve industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CF/Peek with interlayer shear strength and flexural strength and preparation method thereof
  • CF/Peek with interlayer shear strength and flexural strength and preparation method thereof
  • CF/Peek with interlayer shear strength and flexural strength and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] There is the preparation method of the CF / PEEK of interlayer shear strength and flexural strength, and the steps are as follows:

[0053] (1) Sinter 3K5 satin fabrics of CF T300 grade at 300°C for 180 minutes to decompose the original sizing agent on the surface;

[0054] (2) In a saturated water vapor environment with a relative humidity of 95.3%, microwave irradiation and ultraviolet light irradiation are carried out on CF simultaneously, and the product is recorded as ACF; the time of microwave irradiation is 30min, and the microwave frequency is 300MHz; the wavelength of ultraviolet light is irradiated 290nm, UV irradiance is 20W / m 2 ;

[0055] (3) Immerse the ACF in the sulfonated polyether ether ketone / dimethyl sulfoxide / carbon nanotube suspension for 120 minutes, take it out and dry it until the water content is 0.48wt.%, to obtain the sizing modified carbon fiber MCF;

[0056]In the sulfonated polyetheretherketone / dimethyl sulfoxide / carbon nanotube suspension,...

Embodiment 2

[0070] There is the preparation method of the CF / PEEK of interlayer shear strength and flexural strength, and the steps are as follows:

[0071] (1) Sinter 3K5 satin fabrics of CF T300 grade at 350°C for 138min to decompose the original sizing agent on the surface;

[0072] (2) In a saturated water vapor environment with a relative humidity of 95.8%, CF is irradiated with microwaves and ultraviolet light at the same time, and the product is recorded as ACF; the time of microwave irradiation is 27min, and the microwave frequency is 820MHz; the wavelength of ultraviolet light is irradiated 299nm, UV irradiance is 50W / m 2 ;

[0073] (3) Immerse the ACF in the sulfonated polyether ether ketone / dimethyl sulfoxide / carbon nanotube suspension for 115 minutes, take it out and dry it until the water content is 0.45wt.%, to obtain the sizing modified carbon fiber MCF;

[0074] In the sulfonated polyetheretherketone / dimethyl sulfoxide / carbon nanotube suspension, the sulfonated polyether...

Embodiment 3

[0080] There is the preparation method of the CF / PEEK of interlayer shear strength and flexural strength, and the steps are as follows:

[0081] (1) Sinter 5 pieces of satin fabric of T300 grade 3K of CF at 420°C for 5 minutes to decompose the original sizing agent on the surface;

[0082] (2) In a saturated water vapor environment with a relative humidity of 95.9%, CF is irradiated with microwaves and ultraviolet light at the same time, and the product is denoted as ACF; the time of microwave irradiation is 24min, and the microwave frequency is 1GHz; the wavelength of ultraviolet light is irradiated 305nm, UV irradiance is 35W / m 2 ;

[0083] (3) Immerse the ACF in the sulfonated polyether ether ketone / dimethyl sulfoxide / carbon nanotube suspension for 94 minutes, take it out and dry it until the water content is 0.42wt.%, to obtain the sizing modified carbon fiber MCF;

[0084] In the sulfonated polyetheretherketone / dimethyl sulfoxide / carbon nanotube suspension, the sulfonat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to CF / PEEK with high interlaminar shear strength and bending strength and a preparation method of the CF / PEEK. The preparation method comprises the following steps: (1) carryingout high-temperature decomposition on an original sizing agent on the surface of CF; (2) simultaneously carrying out microwave radiation and ultraviolet irradiation on CF in a saturated water vapor environment, and marking a product as ACF; (3) immersing ACF into a sulfonated polyetheretherketone / dimethyl sulfoxide / carbon nanotube suspension, taking out, and drying to obtain sized modified carbonfiber MCF; (4) laminating and hot-pressing the MCF and a PEEK material; and thus obtaining the CF / PEEK with high interlaminar shear strength and bending strength. The bending strength of the finally prepared product is 850-1100 MPa, the bending modulus of the finally prepared product is 55-65 GPa, the interlayer shear strength of the finally prepared product is 95-110 MPa, and the residual compression strength of the finally prepared product after impact is 220-260 MPa. The method disclosed by the invention has the characteristics of high efficiency, environmental friendliness and capability of realizing large-scale production, and the prepared product can replace metal to be applied to the fields of aerospace, medical treatment, machinery, automobiles, rail transit, petroleum transportation and the like.

Description

technical field [0001] The invention belongs to the technical field of carbon fiber reinforced polyether ether ketone (CF / PEEK) composite materials, and relates to a CF / PEEK with interlayer shear strength and bending strength and a preparation method thereof. Background technique [0002] In recent years, thermoplastic composites have attracted extensive attention due to their advantages such as good recyclability, secondary processability, high impact toughness, high specific strength, and high specific modulus. Among various thermoplastic composite materials, CF / PEEK has excellent properties such as high stiffness, high thermal stability, chemical corrosion resistance, wear resistance, and biocompatibility, and is expected to be used as a structural material to replace mature metal or thermosetting composite materials. , Widely used in aerospace, medical, machinery, automobile and rail transportation, oil transportation and other fields. [0003] However, the actual appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/16C08K9/00C08K9/04C08K7/06
CPCC08K7/06C08K9/00C08K9/08C08L61/16
Inventor 朱姝周剑锋史如静马禹王文翰张玥
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com