High-swelling-degree AFL, preparation method and high-swelling-degree AFL ceramic diaphragm
A technology of ceramic diaphragm and swelling degree, which is applied in the direction of electrical components, non-aqueous electrolyte batteries, circuits, etc., can solve the problems of poor contact, affecting the service life of batteries, and small particle size, so as to reduce the change of size and avoid poor interface contact Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Further, the present invention also provides a method of preparation of high-only-only AFL, including the step of being subjected to immersion in an electrolytic solution to obtain swelling PMMA; stirring in a PAN solution, resulting PAN-coated PMMA; after drying PMMA, it is highlighted AFL.
[0026] Among them, optionally, the PMMA can, but is not limited to, a spherical PMMA having a molecular weight of from 5 to 200,000.
[0027] Alternatively, the temperature of the pMMA is placed in an electrolyte can be carried out, but is not limited to, 40-50 ° C, and the time can be, but not limited to, 24-72 h, so that PMMA is fully swelling.
[0028] Alternatively, the electrolyte can be of no limitation is a carbonate (PC), vinyl carbonate (EC), diethyl carbonate (DEC) or dimethyl carbonate (DMC).
[0029] Optionally, the temperature of the PN coated PMMA can be, but not limited to, 40-50 ° C to avoid the reduction of the inner layer PMMA.
[0030] Optionally, the molecular weig...
Example Embodiment
[0042] Example 1
[0043] The 20 kg of a molecular weight of 100,000 spherical PMMA was placed in diethyl carbonate for 48 h at 50 ° C to obtain swelling PMMA; stirring the swelling PMMA in a PAN solution of 40% in a PAN solution to obtain a PAN package The coated PMMA; After drying PMMA was dried at 45 ° C, it obtained highlactance AFL.
Example Embodiment
[0044] Example 2
[0045]The 20 kg of a molecular weight of 50,000 spherical PMMA was placed in diethyl carbonate for 72 h at 45 ° C to obtain swelling PMMA; stirring swollen PMMA in a 5 kg solid content of 40% PAN solution to obtain a PAN package The coated PMMA; After drying PMMA was dried at 40 ° C, it obtained high-only-only AFL.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap