Cap agent with light alkaline particle steel coating

A technology of ladle covering agent and alkaline particles, which is applied in the field of ladle covering agent and can solve the problems of specific gravity, secondary oxidation of molten steel, corrosion of alkaline ladle refractory materials, etc.

Inactive Publication Date: 2008-12-31
上海宝谊保温材料有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the basic ladle covering agent used at home and abroad has a relatively large heap density. Although it has a certain ability to absorb inclusions, the insulation effect is not good.
Although the acidic ladle covering agent has a small stack specific gravity and has good thermal insulation performance, it is easy to cause secondary oxidation of molten steel, and the acidic covering agent will corrode the basic ladle refractory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0005] Embodiment 1: get SiO 2 25kg, CaO 31kg, MgO 10kg, Al 2 o 3 7.5 kg, Fe 2 o 3 1.5 kg, 25 kg of fixed carbon. Mix and stir to form a 100 kg mixture, add an appropriate amount of water, mix well, make granules of Φ8-10mm×8-25mm by extrusion granulation, bake until the moisture content is less than 1%, and pack after sieving.

Embodiment 2

[0006] Embodiment 2: take SiO 2 22 kg, CaO 33 kg, MgO 11 kg, Al 2 o 3 7 kg, Fe 2 o 3 1 kg, 26 kg of fixed carbon. Mix and stir to form a 100 kg mixture, add an appropriate amount of water, mix well, make granules of Φ8-10mm×8-25mm by extrusion granulation, bake until the moisture content is less than 1%, and pack after sieving. When used, the covering agent quickly forms a three-layer structure after being added to the ladle. Due to the small specific gravity of the covering agent, it has good thermal insulation performance; and it contains high fixed carbon, and the heat generated by its chemical reaction can further compensate for the heat loss of molten steel and improve the thermal insulation effect; due to the low content of reducible oxides, It can prevent secondary oxidation of molten steel; since the covering agent is alkaline, it will not corrode the basic refractory material of the ladle, which is beneficial to prolong the ladle life of the ladle.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

A light-weight alkaline particle used as the covering agent of steel ladle contains siO2 (18-26 Wt%), CaO (26-34), MgO (6-12), Al2O3 (5-8), Fe2O3 (0.5-2.0), and stabilized C (18-26). Its advantages are low specific bulk weight, high insulating performance, and high effect to prevent oxidization of molten steel and decrease the corrosion to refractory of ladle.

Description

technical field [0001] The invention relates to a ladle covering agent, in particular to a light alkaline particle ladle covering agent. Background technique [0002] At present, the basic ladle covering agent used at home and abroad has a relatively large heap density. Although it has a certain ability to absorb inclusions, the insulation effect is not good. Although the acidic ladle covering agent has a small stack specific gravity and has good thermal insulation performance, it is easy to cause secondary oxidation of molten steel, and the acidic covering agent will corrode the basic ladle refractory. Contents of the invention [0003] The object of the present invention is to provide an alkaline granular ladle covering agent with low content of reducible oxides and small bulk specific gravity. The present invention designs a light alkaline particle ladle covering agent, which is characterized in that it consists of the following composition and weight percentage: SiO ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111C21C7/076
CPCY02P10/20
Inventor 徐永斌王兆达丁劲光徐兵
Owner 上海宝谊保温材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com