An antique brick and glaze technology, applied in the field of inorganic silicate, can solve the problems of uneven coloring, unnatural transition, and no effective solution, and achieve the effect of bright and diverse colors and uniform glazing.
Inactive Publication Date: 2009-01-21
GUANGDONG NEW ZHONGYUAN CERAMICS
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there are still problems of unnatural transition and uneven coloring when glazed on the surface of the concave-convex blank.
This technical problem has not been effectively resolved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] Take the following raw materials: 20 kg of potassium feldspar, 10 kg of burnt talc, 8 kg of calcite, 12 kg of ball clay, 10 kg of alumina, 10 kg of barium carbonate, 12 kg of burnt kaolin, 0.3 kg of carboxymethyl cellulose, Sodium phosphate 0.5 kg, water 70 kg.
[0013] Preparation process: first ball mill the raw material for 10 hours, and grind it into a slurry with a fineness of 0.1-0.2%; The part content is less than 3wt%, and finally sieved to get 40-100 mesh powder.
Embodiment 2
[0015] Take the following raw materials: 30 kg of potassium feldspar, 15 kg of quartz, 8 kg of burnt talc, 6 kg of calcite, 5 kg of zinc oxide, 10 kg of ball clay, 8 kg of alumina, 8 kg of barium carbonate, 8 kg of burnt kaolin, carboxylate 0.2 kg of methyl cellulose, 0.4 kg of sodium tripolyphosphate, and 70 kg of water.
[0016] Preparation process: first ball mill the raw materials for 10 hours, and grind them into a slurry with a fineness of 0.1-0.2%; The part content is less than 3wt%, and finally sieved to get 40-100 mesh powder.
Embodiment 3
[0018] On the basis of the raw materials of Example 1, add 3 kilograms of red material.
[0019] Preparation process: first ball mill the raw materials for 10 hours, and grind them into a slurry with a fineness of 0.1-0.2%; The part content is less than 3wt%, and finally sieved to get 40-100 mesh powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
A dry enamel for pseudo-classical brick is prepared proportionally from potash feldspar, quartz, calcined talc, calcite, Zinc oxide, spherical earth, aluminum oxide, barium carbonate, clacined kaolinite, carboxymethyl cellulose, sodium tripolyphosphate and water through ball grinding, spray pulverizing and sieving.
Description
technical field [0001] The invention relates to the technical field of inorganic silicates, in particular to a dry glaze for antique bricks. technical background [0002] Generally, glaze is a material with high strength and high viscosity prepared by water, pigment, binder and glaze base formula. It can make ceramic products have rich colors and beautiful appearance, so they are very popular in the market. However, there are still problems such as unnatural transition and uneven coloring when glazing is applied to the surface of the concave-convex blank. This technical problem has not been effectively resolved. Contents of the invention [0003] The object of the present invention is to provide a dry glaze for archaize bricks. [0004] In order to realize above-mentioned purpose of the invention, technical scheme of the present invention is: [0005] It is obtained by ball milling the following raw materials in parts by weight, spraying powder and sieving: 20-40 parts...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More