Fiberglass radome modified by PE micro powder and preparation method thereof

A fiberglass radome and micropowder technology, applied in the direction of the radiation unit cover, can solve the problem of high DK value, achieve the effect of low DK value, simple preparation method, and good wave transmission performance

Active Publication Date: 2013-01-30
NANJING HUAGE ELECTRONICS & AUTOMOBILE PLASTIC IND
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If PE micropowder can be used to modify FRP radome, it can solve the problem of high DK value of existing FRP radome products. After countless experiments, the inventor finally successfully developed a FRP radome modified with PE micropowder. Formula and processing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiberglass radome modified by PE micro powder and preparation method thereof
  • Fiberglass radome modified by PE micro powder and preparation method thereof
  • Fiberglass radome modified by PE micro powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Ingredients: 100kg of unsaturated polyester (A402-972), 15kg of PE micropowder, 2kg of pigment paste (RAL7035), 1kg of release agent, 1kg of curing agent, 1kg of accelerator. The dielectric constant of the tested product is shown in Table 1.

Embodiment 2

[0023] Raw material formula: 100kg of unsaturated polyester (A409-972), 12kg of PE micropowder, 2kg of pigment paste (RAL4008), 1kg of release agent, 1kg of curing agent, and 1kg of accelerator. The dielectric constant of the tested product is shown in Table 1.

Embodiment 3

[0025] Raw material formula: 100kg of unsaturated polyester (A402-902), 10kg of PE powder, 1kg of pigment paste (RAL 3011), 1kg of release agent, 1kg of curing agent, 1kg of accelerator. The dielectric constant of the tested product is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fiberglass radome modified by PE micro powder, which reduces the DK value thereof, and improves the wave penetration performance of the products. The fiberglass radome modified by PE micro powder is prepared by the following raw materials in weight portion: 100 portions of unsaturated polyester, 3-15 portions of PE micro powder, 0.5-2 portions of mold release agent, 0.5-2 portions of curing agent and 0.5-2 portions of accelerator.

Description

Technical field [0001] The invention relates to a glass fiber reinforced plastic antenna cover and a preparation method thereof, and more specifically to a glass fiber reinforced plastic antenna cover modified with PE micropowder and a preparation method thereof. Background technique [0002] Due to the advantages of good weather resistance, insulation, light weight, high strength, stable size and high production efficiency, FRP radome has been widely used in many fields such as the protective housing of wireless and mobile communication base station antennas. Those of ordinary skill in the art know that glass fiber reinforced plastic radomes are made of glass fiber plus auxiliary materials (impregnated materials). Since glass fiber is relatively stable, the modification of glass fiber reinforced plastic radome is generally to modify the auxiliary materials to achieve glass fiber reinforced plastics. The performance requirements of the radome; for example, the relevant content of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01Q1/42C08L67/06C08L23/06B29C47/92B29C48/92
CPCB29C48/9185B29C48/04B29C48/92B29C2948/9258B29C2948/92704B29C2948/92895B29C2948/92933
Inventor 李庆喜叶枫韬
Owner NANJING HUAGE ELECTRONICS & AUTOMOBILE PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap