A magnesium alloy, high-performance technology, applied in the field of integrated complete equipment for high-strength deformed magnesium alloy parison continuous casting production, can solve problems such as continuous casting operation time conflicts
Active Publication Date: 2010-05-19
武汉镁里镁科技有限公司
View PDF3 Cites 9 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In the above patent report, it is not stated how to prevent the oxidation and combustion of magnesium alloys by charging the hot furnace; how to deal with the residual magnesium alloys after the shutdown of the furnace; how to solve the time conflict between the smelting operation of a single melting furnace and the continuous casting operation
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment approach
[0008] The following measures are taken for the above purposes, that is, vacuum protection is used throughout the process, including the addition of raw materials in the furnace, the melting and preparation of magnesium alloy materials, the buffering of the heat preservation and homogenization furnace to ensure that the melting operation and continuous casting operation are synchronized in time, and the modification of liquid materials It works in a closed environment without external interference, and achieves the design goal of no pollution in the whole process. In addition, the raw materials used in the present invention do not refer to traditional casting master alloys and working alloys, but to use the lowest-end basic materials as far as possible, such as pure magnesium, a small amount and a small amount of supplementary pure metal or alloy materials, to reduce energy consumption and reduce pollution. link.
[0009] The present invention is characterized in that 1. feedi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| tensile strength | aaaaa | aaaaa |
| elongation | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a high-performance magnesium alloy parison continuous casting production line and relates to the technical fields of vacuum magnesium alloy metallurgy and material preparation. The production line is used for producing high-strength deformation magnesium alloy parison materials by whole-course vacuum protection. Equipment for the production line is provided with two vertical melting furnaces used for melting magnesium medium alloy or working alloy, wherein each melting furnace is divided into the two following parts in space: a hermetic melting chamber and a hermetic furnace body; and the pressure of the furnace body is lower than that of the melting chamber so as to form a vacuum barrier and double vacuum protection melting. Feeding cabins are arranged above furnace covers of the melting furnaces, and the opening and closing of doors of the cabins is matched with the conversion of pressure in the cabins so as to eradicate oxidization and burning of magnesium during feeding materials into hot furnaces. A heat insulation and homogenization furnace is arranged between the two melting furnaces to mix liquid coming from the melting furnaces and prepare magnesium alloy containing target components, and then the heat insulation and homogenization furnace stand still to preserve heat. An inoculation agent and leavening agent flowing addition mechanism is arranged on a gap bridge so as to effectively increase cores and prevent recession. Magnetic stirring is carried out in a crystallization process to control the pressing force and the traction speed of a tractor in real time. The equipment has compact structure, safe production and no pollution.
Description
Technical field: [0001] The invention relates to the technical field of vacuum magnesium alloy metallurgy and the technical field of material preparation, in particular to an integrated complete set of equipment for continuous casting of high-strength deformed magnesium alloy blanks. Background technique: [0002] The use of high-strength and high-ductility magnesium alloy forgings in the fields of automobiles and motorcycles has been widely valued. Facing the demand for a large number of blank materials for magnesium alloy forgings, it is hoped that the melting, liquid modification, and solidification of magnesium alloys Advanced technologies for process integration such as liquefaction and continuous casting. However, due to the high vapor pressure of magnesium, the problem of flammability, explosion and oxidation in the melting of magnesium alloys is particularly prominent, so the protection of magnesium alloy melts has always been highly valued by people. [0003] In or...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/14
Inventor 王仁辉
Owner 武汉镁里镁科技有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap