Cobalt-based amorphous alloy wire and preparation method thereof

An amorphous alloy and cobalt-based technology, which is applied in the field of cobalt-based amorphous alloy wire and its preparation, can solve problems such as no substantive breakthroughs, achieve excellent mechanical properties and soft magnetic properties, large amorphous forming ability, and facilitate The effect of the operation

Active Publication Date: 2011-12-28
NINGBO INNOVATION CENT FOR APPLIED MAGNETICS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country has also been carrying out related research, but so far no substantial breakthroughs have been made

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cobalt-based amorphous alloy wire and preparation method thereof
  • Cobalt-based amorphous alloy wire and preparation method thereof
  • Cobalt-based amorphous alloy wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The molecular formula of the cobalt-based amorphous alloy wire of this example is Co 64.8 Fe 7.2 Si 4.8 B 19.2 Nb 4 , the preparation steps are as follows: prepare 20 g of raw materials Co, Fe, B, Si and Nb with a purity greater than 99% according to the composition of the cobalt-based amorphous alloy wire of this embodiment, and then use a high-frequency induction melting furnace to melt under the protection of argon , the melting current is 6.5A, and the melting time is 12 minutes;

[0028] Break the smelted alloy ingot into small pieces of about 2g, put it into a glass test tube, connect the glass test tube to the vacuum system, repeatedly vacuumize 2 to 3 times, and then fill the glass test tube with argon gas at 1 atmosphere. And adjust the height of the cooling water so that it is 5-15 mm away from the bottom of the test tube, and at the same time adjust the appropriate current to melt the alloy. When the glass in contact with the molten alloy softens, pull ou...

Embodiment 2

[0032] The molecular formula of the cobalt-based amorphous alloy wire of this example is Co 63.1 Fe 3.9 Si 5.6 B 22.4 Nb 5 . The preparation steps are as follows: prepare 20 g of raw materials Co, Fe, B, Si and Nb with a purity greater than 99% according to the composition of the cobalt-based amorphous alloy wire in this embodiment, and then use a high-frequency induction melting furnace to melt under the protection of argon. The melting current is 7.0A, and the melting time is 10 minutes;

[0033] Break the smelted alloy ingot into small pieces of about 2g, put it into a glass test tube, connect the glass test tube to the vacuum system, repeatedly vacuumize 2 to 3 times, and then fill the glass test tube with argon gas at 1 atmosphere. And adjust the height of the cooling water so that it is 5-15mm away from the bottom of the test tube. At the same time, adjust the appropriate current to melt the alloy. When the glass in contact with the molten alloy softens, pull out a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cobalt-based amorphous alloy wire and a preparation method thereof. The molecular formula of the alloy is CoaFebBcSidNbe, wherein a=60-70%, b=2-10%, c=15-25%, d=3- 6%, e=2~6%, and a+b+c+d+e=100%, its preparation method is to adopt the glass coating spinning method, and the cobalt-based amorphous silk material prepared has excellent soft magnetic properties In addition to its energy and mechanical properties, it also has a very high rate of change of giant magnetoresistance and magnetic field sensitivity. The invention can greatly improve the giant magnetoresistance change rate and magnetic field sensitivity of the cobalt-based amorphous wire, and the product performance is better than the current domestic products of the same type, and can be widely used in the fields of AC sensor technology and magnetic sensor technology.

Description

technical field [0001] The invention relates to a cobalt-based amorphous alloy wire and a preparation method thereof, and belongs to the technical field of magnetic sensitive sensors, magnetic materials and preparation thereof. Background technique [0002] The amorphous state refers to a state in which the material has no time to crystallize during the rapid cooling and solidification process, and the atomic arrangement maintains the short-range order and long-range disorder of liquid metal. Due to the lack of long-range atomic order, compared with traditional crystalline alloy materials, amorphous alloys exhibit many excellent properties, such as good mechanical properties, strong corrosion resistance, and unique magnetoelectric properties, etc. This makes amorphous alloys show a wide range of application prospects. [0003] As a magnetic material, amorphous soft magnetic alloys not only have excellent soft magnetic properties, such as high magnetic permeability, low coer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C45/04C22C1/02
Inventor 沈宝龙宁伟蔡平平
Owner NINGBO INNOVATION CENT FOR APPLIED MAGNETICS CO LTD