Special resin for solar film and preparation method thereof

A technology of solar film and resin, which is applied to the resin of solar film for architectural glass and the field of making automobile window glass, which can solve the problems of high cost, poor heat insulation effect, complicated production process of solar film, etc., and achieve improved heat insulation effect , good film-forming performance, and the effect of reducing production costs

Active Publication Date: 2012-08-08
QINGDAO HAOCHENG INDAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a low-cost, good effect of blocking ultraviolet rays and infrared rays, remarkable heat insulation effect, impact resistance strength and stability for the problems of existing solar film production processes such as complex production process, high cost, and poor heat insulation effect. High special resin for solar film and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special resin for solar film and preparation method thereof
  • Special resin for solar film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0026] Specific embodiment one: a kind of special resin of new solar film, its raw material composition is by weight: 3 parts of polyvinyl alcohol, 1.5 parts of n-butyraldehyde, 0.15 part of ethanol, 0.06 part of pigment, 0.3 part of reagent grade hydrochloric acid, alkaline auxiliary 0.3 parts of agent, 0.1 part of dispersant, 0.015 parts of ultraviolet blocking agent, 0.015 parts of infrared blocking agent, 0.03 parts of antioxidant, 30 parts of pure water.

[0027] The steps of its specific preparation method are:

[0028] (1) dissolve

[0029] Add 30 parts of pure water into the reactor, start the agitator, slowly put 3 parts of polyvinyl alcohol into the reactor, start heating to 95-99°C, and keep it warm for 4-6 hours to ensure that the polyvinyl alcohol is completely dissolved;

[0030] (2) Reaction

[0031] Lower the temperature of the solution to room temperature (20-25°C), add 1.5 parts of butyraldehyde to the polyvinyl alcohol solution, and stir for 5 minutes; the...

specific Embodiment 2

[0036] Concrete embodiment two: a kind of novel solar film special resin, its raw material composition is by weight: 4 parts of polyvinyl alcohol, 2 parts of n-butyraldehyde, 0.2 part of ethanol, 0.07 part of pigment, 0.4 part of reagent grade hydrochloric acid, alkaline auxiliary 0.4 part of agent, 0.1 part of dispersant, 0.02 part of ultraviolet blocking agent, 0.02 part of infrared blocking agent, 0.04 part of antioxidant, 40 parts of pure water.

[0037] The steps of its specific preparation method are:

[0038] (1) dissolve

[0039] Add 40 parts of pure water to the reactor, start the agitator, slowly put 4 parts of polyvinyl alcohol into the reactor, start heating to 95-99°C, and keep it warm for 4-6 hours to ensure that the polyvinyl alcohol is completely dissolved;

[0040] (2) Reaction

[0041] Lower the solution temperature to normal temperature (20-25°C), add 2 parts of butyraldehyde to the polyvinyl alcohol solution, stir for 5 minutes; Slowly and evenly add ant...

specific Embodiment 3

[0046] Specific embodiment three: a kind of special resin of new solar film, its raw material composition is by weight: 5 parts of polyvinyl alcohol, 2.5 parts of n-butyraldehyde, 0.25 part of ethanol, 0.08 part of pigment, 0.5 part of reagent grade hydrochloric acid, alkaline auxiliary 0.5 parts of agent, 0.3 parts of dispersant, 0.025 parts of ultraviolet blocking agent, 0.025 parts of infrared blocking agent, 0.05 parts of antioxidant, 50 parts of pure water.

[0047] The steps of its specific preparation method are:

[0048] (1) dissolve

[0049] Add 50 parts of pure water into the reactor, start the agitator, slowly put 3 parts of polyvinyl alcohol into the reactor, start heating to 95-99°C, and keep it warm for 4-6 hours to ensure that the polyvinyl alcohol is completely dissolved;

[0050] (2) Reaction

[0051] Lower the solution temperature to normal temperature (20-25°C), add 2.5 parts of butyraldehyde to the polyvinyl alcohol solution, stir for 5 minutes; Slowly a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to special resin for a solar film and a preparation method thereof, wherein the special resin comprises the following raw materials in parts by weight: 3-5 parts of polyvinyl alcohol, 1.5-2.5 parts of butyraldehyde, 0.15-0.25 part of ethanol, 0.015-0.025 part of ultraviolet obstructing agent, 0.015-0.025 part of infrared obstructing agent, 0.1-0.3 part of dispersant, 0.06-0.08 part of pigment, 0.03-0.05 part of antioxidant, 0.3-0.5 part of reagent-grade hydrochloric acid, 0.3-0.5 part of alkaline auxiliary agent and 30-50 parts of pure water. The invention realizes the action of blocking ultraviolet rays and infrared rays, can achieve 99 percent of obstruction rate and has the advantages of high anti-impact strength and stability and good film-forming performance; and the reaction is carried out at normal temperature, therefore, the production cost is lowered. The solar film made of the special resin can be widely applied to the glass for automobile windows, building windows, and the like; and compared with like products, the heat insulating effect of the solar film made of the special resin is markedly improved under the condition of identical light transmittance index.

Description

technical field [0001] The invention relates to a resin for solar film, in particular to a resin for making solar film for automobile window glass and building glass. Background technique [0002] At present, there are many solar film products in the international market, and the requirements for solar film materials generally have the characteristics of light blocking, heat insulation, and certain decorative effects. The existing solar film products are mainly products from the United States, South Korea, and Taiwan. For example, the most used big brand products include: Long film, Weigu solar film, Federation Suntech solar film and Johnson & Johnson solar film. The solar film of these big brands Although the film products can achieve 99% ultraviolet and infrared blocking rate, the production process of solar film is complicated, and the price is high, the cost is high, and the heat insulation effect is not very ideal. There are hundreds of solar film brands in the domesti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L29/14C08F16/38
Inventor 李金伟吴进来张美玲尹凤李克元张培华张琪
Owner QINGDAO HAOCHENG INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com