An Improved Anti-aging Waterproof Coating

A waterproof coating and anti-aging technology, applied in the coating and other directions, can solve the problems of low strength and low self-protection, and achieve the effects of good anti-aging performance, good waterproof effect and convenient construction.

Inactive Publication Date: 2016-05-25
南京施美特防水材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that its strength is not high and its self-protection is not strong.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The invention is an improved anti-aging waterproof coating, which is made of the following raw materials in parts by weight:

[0011] 8 parts of fluoroolefin resin, 3.2 parts of 4-methylguaiacol, 4.8 parts of ethylene glycol, 5.5 parts of white latex, 2.7 parts of propylene glycol methyl ether acetate, 2.2 parts of trimethylolpropane triacrylate, 2,5 - 3.2 parts of di-tert-butyl hydroquinone and 2.8 parts of aluminum carbon refractory brick powder.

Embodiment 2

[0013] The invention is an improved anti-aging waterproof coating, which is made of the following raw materials in parts by weight:

[0014] 5 parts of fluoroolefin resin, 2.5 parts of 4-methylguaiacol, 3.5 parts of ethylene glycol, 2.5 parts of white latex, 1.2 parts of propylene glycol methyl ether acetate, 1.2 parts of trimethylolpropane triacrylate, 2,5 - 1.5 parts of di-tert-butyl hydroquinone and 2.3 parts of aluminum carbon refractory brick powder.

Embodiment 3

[0016] The invention is an improved anti-aging waterproof coating, which is made of the following raw materials in parts by weight:

[0017] 10 parts of fluoroolefin resin, 3.8 parts of 4-methylguaiacol, 8 parts of ethylene glycol, 7 parts of white latex, 3.5 parts of propylene glycol methyl ether acetate, 2.8 parts of trimethylolpropane triacrylate, 2,5 - 3.6 parts of di-tert-butyl hydroquinone and 3.8 parts of aluminum carbon refractory brick powder.

[0018] The waterproof coating of the present invention, because aluminum-carbon refractory brick powder is added therein, there is a density difference between such aluminum-carbon refractory brick powder and other components, when the waterproof coating of the present invention is applied to the waterproof surface, the aluminum in the waterproof coating Carbonaceous refractory brick powder will be distributed in layers due to different densities, which can have the same waterproof effect as "two felts and three oils"; the raw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an improved aging-resistant waterproof coating material. The improved aging-resistant waterproof coating material is prepared from the following raw materials in parts by weight: 5-10 parts of fluoro-olefin resin, 2.5-3.8 parts of 4-methyl guaiacol, 3.5-8 parts of glycol, 2.5-7 parts of white latex, 1.2-3.5 parts of propylene glycol methylether acetate, 1.2-2.8 parts of trimethylol propane triacrylate, 1.5-3.6 parts of 5-di-tert-butyl-hydroquinone and 2.3-3.8 parts of aluminum-carbon firebrick powder. According to the waterproof coating material disclosed by the invention, the aluminum-carbon firebrick powder is added, and density differences exist between the aluminum-carbon firebrick powder and other ingredients, so that when the waterproof coating material disclosed by the invention is coated on a waterproof surface, the aluminum-carbon firebrick powder in the waterproof coating material can be of layered distribution due to different densities and can exert a waterproof effect like that of two-felt three-oil; a finished product of the waterproof coating material has the advantages of convenience in construction, strong bonding power and tensile resistance and good ageing resistance.

Description

technical field [0001] The invention relates to an improved anti-aging waterproof paint, which belongs to the field of building materials. Background technique [0002] At present, the waterproofing of various buildings is a key issue. Commonly used waterproof materials are various types of waterproof membranes, waterproof coatings, waterproof cement, etc. Waterproof membranes are generally hot construction, mostly baked by fire, the main disadvantage is that the bonding is not comprehensive, there are seams, and some special parts, such as corners, nozzles, etc. Not easy to repair. Waterproof coatings are usually applied cold. After the waterproof coating is mixed well, it can be painted at one time. There is no joint construction and strong adhesion. Its shortcoming is that strength is not high, and self-protection is not strong. Contents of the invention [0003] Aiming at the deficiencies of the existing technology, the technical problem to be solved by the present...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12C09D5/00
Inventor 王玉庆
Owner 南京施美特防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com