Multi-layer composite wear-resistant decompression pipe and preparation method thereof

A multi-layer composite and decompression pipe technology, applied in the field of wear-resistant pipes, can solve the problems of easy loosening of ceramic pipes and metal pipes, low strength of wear-resistant pipes, and high production difficulty, achieving excellent durability, convenient preparation, Effect of good micro-expansion properties

Active Publication Date: 2015-10-21
曹海亮
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides a multi-layer composite wear-resistant decompression pipe and a preparation method thereof, which solve the technical problems that the existing wear-resistant pipe has low strength, difficult manufacture, easy loosening and cracking between the ceramic pipe and the metal pipe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-layer composite wear-resistant decompression pipe and preparation method thereof
  • Multi-layer composite wear-resistant decompression pipe and preparation method thereof
  • Multi-layer composite wear-resistant decompression pipe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0048] Examples see figure 1 , figure 2 As shown, this multi-layer composite wear-resistant decompression pipe is composed of wear-resistant ceramic inner layer 1, micro-expansion bonding layer 2 and metal outer layer 3 sequentially from the inside to the outside.

[0049] The multi-layer composite wear-resistant decompression pipe is sequentially composed of a diameter-reducing section 4, a straight pipe section 5, and a diameter-expanding section 6 from the inlet end to the outlet end, and the metal outer layer 3 at the inlet end and the outlet end is respectively provided with an inlet connecting flange 3.1 and outlet connection flange 3.2.

[0050] The multi-layer composite wear-resistant decompression pipe is a segmented composite structure, and each segment of the segmented composite structure is connected to each other by segmented connecting flanges 3.3 on the metal outer layer 3 . The multi-layer composite wear-resistant decompression pipe can also be an integral s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multi-layer composite wear-resistant pressure reduction pipe and a manufacturing method of the multi-layer composite wear-resistant pressure reduction pipe. The multi-layer composite wear-resistant pressure reduction pipe is sequentially formed by a wear-resistant ceramic inner layer, a micro-expansion combination layer and a metal outer layer from inside to outside in a composite mode. The multi-layer composite wear-resistant pressure reduction pipe sequentially comprises a diameter reduction section, a straight pipe section and a diameter increasing section from the inlet end to the outlet end, and the portion, located at the inlet end, of the metal outer layer and the portion, located at the outlet end, of the metal outer layer are provided with an inlet connecting flange and an outlet connecting flange respectively. The wear-resistant ceramic inner layer, the combination layer and the metal outer layer are seamlessly combined, integrality of the product is embodied, and the phenomenon that the inner layer and the outer layer are loosened can not occur. The ceramic layer can be made of zirconia toughened alumina ceramic, and excellent durability of the product is achieved due to the rigidity and wear resistance of the product. The inner layer ceramic material, the combination layer and the outer layer metal material are firmly combined together due to the micro-expansion combination layer through the adhering action and the micro-expansion action. The multi-layer composite wear-resistant pressure reduction pipe can be of a multi-section combination structure, and therefore a pipeline can be conveniently manufactured, and machining accuracy of the pipeline is improved.

Description

technical field [0001] The invention relates to a wear-resistant pipeline used in coal-to-oil production and a preparation method for the wear-resistant pipeline. Background technique [0002] Abrasion-resistant decompression pipe is a kind of coal slag conveying pipe widely used in coal-to-liquids production line. In order to improve the wear resistance and corrosion resistance of metal conveying pipes, the existing technology is mainly to make ceramic and metal composite pipes. The existing ceramic and metal composite pipe production processes mainly include the following two types: [0003] 1. Paste tiles on the inner wall of metal pipes. This product has the following deficiencies in use: [0004] 1. The pasted tiles have no integrity and are easy to fall off; [0005] 2. Can not transport large particles; [0006] 3. Can not be impacted; [0007] 4. Combination splicing is difficult to make. [0008] 2. Coating adhesive on the outer wall of the ceramic pipe or coat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16L9/14C04B28/14B28B21/72
CPCB28B21/72C04B28/14F16L9/14C04B24/2623C04B22/142C04B22/064C04B22/066C04B22/06C04B14/106C04B14/12C04B24/26C04B24/04C04B24/30
Inventor 曹海亮曹海涛
Owner 曹海亮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com