Multi-layer co-extruded cast film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A multi-layer co-extrusion, cast film technology, applied in the direction of lamination, layered products, lamination devices, etc., can solve the problems of water vapor generation, affecting light transmission and aesthetics, and inability to reuse
Active Publication Date: 2017-04-19
中塑新材料科技(杭州)有限公司
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In the prior art, when it is used to package food, especially fresh fruit, since the pulp cells of the fruit are still respiration, water vapor will be generated in the package, which will affect the light transmittance and aesthetics
At the same time, when people need to take out food, they often choose to pierce the sealing film on the packaging box instead of tearing the sealing film on the packaging box, which causes the damage of the sealing film and cannot be reused.
The reason is that the sealing film and the packaging box are highly bonded, and it is far more difficult for people to tear off the sealing film on the packaging box than to pierce the sealing film on the packaging box.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0040] (1) In parts by weight, take 30 parts of hydrogenated C5 petroleum resin and add it into a reactor whose temperature is controlled at 120° C. After the material is melted, add 15 parts of paraffin, and control the rotating speed at 150 rad / min to start stirring until the sample is completely melted;
[0041] (2) Raise the temperature to 160°C, continue to stir for 0.5h, and then evenly add EVA resin to the reactor several times within 1.5h;
[0042] (3) Add calcium carbonate, control the rotation speed to 200rad / min, stir at a constant speed until uniform, and the glue comes out.
Embodiment 2
[0044] (1) In parts by weight, take 35 parts of hydrogenated C5 petroleum resin and add it into a reactor whose temperature is controlled at 120° C. After the material is melted, add 7 parts of paraffin, and control the rotating speed at 100 rad / min to start stirring until the sample is completely melted;
[0045] (2) Raise the temperature to 160°C, continue stirring for 1 hour, and then evenly add EVA resin to the reactor several times within 1.5 hours;
[0046] (3) Add calcium carbonate, control the rotation speed to 100rad / min, stir at a constant speed until uniform, and the glue comes out.
Embodiment 3
[0048] (1) In parts by weight, take 40 parts of hydrogenated C5 petroleum resin and add it into a reactor whose temperature is controlled at 120° C. After the material is melted, add 10 parts of paraffin, and control the rotating speed at 125 rad / min to start stirring until the sample is completely melted;
[0049] (2) Raise the temperature to 160°C, continue stirring for 1 hour, and then evenly add EVA resin to the reactor several times within 1.5 hours;
[0050] (3) Add calcium carbonate, control the rotation speed to 125rad / min, stir at a constant speed until uniform, and glue comes out.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a multi-layer coextrusion cast film which is formed by 11 layers of resin beds has the structure expression as follows: N1 / B1 / C / N2 / D1 / N3 / D2 / N4 / A / N5 / B2, wherein A is anticorrosive coating, B1 and B2 are sealing layers, C is an anti-fracture layer, D1 and D2 are compression resistant layers, N1, N2, N3, N4 and N5 are glue adhering layers, A is polypropylene, B1 and B2 are ethylene-vinyl alcohol copolymers, C is polyamide, D1 and D2 are polyethylene glycol terephthalate, and N1, N2, N3, N4 and N5 are EVA hot melt glue. The multi-layer coextrusion cast film has the beneficial effects that while the sealing state is guaranteed, a sealing film is tightly laminated with a packaging box so as to prevent air from entering; while content in the packaging box needs to be taken out, the sealing film can be conveniently torn from the packaging box without causing breaking of the sealing film, and no residue of the sealing film exists at the original adhesion part of the sealing film and the packaging box. Meanwhile, the sealing film has an anti-fogging function, so that the packaging box has good light transmission property and attractiveness.
Description
technical field [0001] The present invention relates to a film, and more particularly to a multilayer coextruded cast film. Background technique [0002] The extrusion casting process has the advantages of fast production speed, low cost, high output, etc., and the produced film has many advantages such as good surface performance, good transparency, good gloss, and uniform thickness. At the same time, post-treatment of the film such as corona, Printing and other processes are simple, because it is widely used in various industries such as textile products, food, daily necessities, medical supplies and flower packaging. [0003] There are many varieties of cast film, which can be divided into single-layer film and multi-layer film according to their structure. With the continuous development of the food packaging industry, the performance requirements of packaging materials are getting higher and higher, which makes the market demand for multilayer films continue to increas...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 