Preparation technology of tempered vacuum laminated glass for automobile

A preparation process, laminated glass technology, applied in chemical instruments and methods, lamination devices, lamination, etc., to achieve the effects of strong bonding force, high bonding strength, and convenient operation of the production process

Inactive Publication Date: 2016-09-28
戴婷婷
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the rapid development of the automobile industry, the continuous improvement of road conditions and the continuous improvement of people's requirements for driving safety and driving comfort, the original automobile glass problems have been exposed and can no longer meet many new requirements, which has accelerated the research and development of new automotive glass products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A preparation process for tempered vacuum laminated glass for automobiles, comprising the steps of:

[0036] (1) Preparation of vacuum flat glass; including the following steps:

[0037] (1a) Glass cutting process: it is completed by a glass scribing machine, which is designed as a hydraulic double-cylinder two-way scribing glass, which slits the glass from two directions perpendicular to each other, and the glass scribing knife is adjusted according to the required glass size;

[0038] (1b) Cleaning and drying process: the automatic cleaning and drying machine completes the four operations of generating ionized water, rinsing the glass surface with ionized water, automatically drying, and drying;

[0039] (1c) Placing the support column process: After cleaning, one piece of glass is coated, and one piece is punched. First, the formed support is placed in the design template, and the lack of columns is controlled by the camera, and then the template is moved to 1cm abov...

Embodiment 2

[0056] A preparation process for tempered vacuum laminated glass for automobiles, comprising the steps of:

[0057] (1) Preparation of vacuum flat glass; including the following steps:

[0058] (1a) Glass cutting process: it is completed by a glass scribing machine, which is designed as a hydraulic double-cylinder two-way scribing glass, which slits the glass from two directions perpendicular to each other, and the glass scribing knife is adjusted according to the required glass size;

[0059] (1b) Cleaning and drying process: the automatic cleaning and drying machine completes the four operations of generating ionized water, rinsing the glass surface with ionized water, automatically drying, and drying;

[0060] (1c) Placing the support column process: After cleaning, one piece of glass is coated, and one piece is punched. First, the formed support is placed in the design template, and the lack of columns is controlled by the camera, and then the template is moved to 1cm abov...

Embodiment 3

[0077] A preparation process for tempered vacuum laminated glass for automobiles, comprising the steps of:

[0078] (1) Preparation of vacuum flat glass; including the following steps:

[0079] (1a) Glass cutting process: it is completed by a glass scribing machine, which is designed as a hydraulic double-cylinder two-way scribing glass, which slits the glass from two directions perpendicular to each other, and the glass scribing knife is adjusted according to the required glass size;

[0080] (1b) Cleaning and drying process: the automatic cleaning and drying machine completes the four operations of generating ionized water, rinsing the glass surface with ionized water, automatically drying, and drying;

[0081] (1c) Placing the support column process: After cleaning, one piece of glass is coated, and one piece is punched. First, the formed support is placed in the design template, and the lack of columns is controlled by the camera, and then the template is moved to 1cm abov...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation technology of tempered vacuum laminated glass for an automobile. The preparation technology comprises the following steps: firstly preparing vacuum plate glass and a laminated glass film, and washing and drying the vacuum plate glass, wherein the temperature of washing water is 25 to 45 DEG C; washing outsourcing tempered glass through a glass washing machine, and putting the outsourcing tempered glass on a working platform after drying; drying the laminated glass film through a washing and drying machine, and strictly inspecting the laminated glass film before putting the laminated glass film in the vacuum plate glass; cutting a prepared film on a table under which a lighting lamp is arranged according to a sample plate; carrying out a closing process on the working platform by adopting a manual way; putting the vacuum plate glass and the tempered glass which are closed in a vacuum furnace, firstly vacuumizing and heating the vacuum furnace, rapidly rising the temperature to 60 to 70 DEG C, and keeping warm for 20 to 30 minutes; stopping heating, and slowing cooling the temperature in the vacuum furnace; closing the vacuum pump when the temperature of the vacuum furnace is up to normal temperature; placing novel glass after solidification under room temperature for a certain time, and fully cooling and solidifying the novel glass, thus obtaining a finished product.

Description

technical field [0001] The invention relates to the technical field of tempered glass preparation, in particular to a preparation process of tempered vacuum laminated glass for automobiles. Background technique [0002] Tempered glass (Tempered glass / Reinforced glass) belongs to safety glass. Tempered glass is actually a kind of prestressed glass. In order to improve the strength of glass, chemical or physical methods are usually used to form compressive stress on the glass surface. Wind pressure, cold and heat, impact, etc. Pay attention to distinguish it from FRP. The development of toughened glass can be traced back to the middle of the 17th century. There was a Rhine prince named Robert who once did an interesting experiment. He put a drop of molten glass in ice-cold water, and finally made a kind of tempered glass. Extremely hard glass. This high-strength granular glass is like water droplets, dragging a long and curved tail, called "Prince Robert granules". But wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C27/10C03C27/12B32B37/06
CPCC03C27/10B32B37/06B32B2307/306B32B2307/412
Inventor 戴婷婷
Owner 戴婷婷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap