Compound pseudo-ginseng, kaolin and bamboo fiber hemostatic gauze and preparation method thereof

A technology of hemostatic gauze and compound notoginseng, which is applied in blood diseases, medical formulas, medical preparations containing active ingredients, etc., can solve the problems of no effective compound hemostatic gauze and retention, and achieve good hemostatic effect and stable properties , the effect of not easy to fall off

Inactive Publication Date: 2016-10-26
WUHAN GENERAL HOSPITAL OF GUANGZHOU MILITARY
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hemostatic gauze used for first aid in China is still at the level of non-woven gauze, and there is no effective composite hemostatic gauze for emergency use so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound pseudo-ginseng, kaolin and bamboo fiber hemostatic gauze and preparation method thereof
  • Compound pseudo-ginseng, kaolin and bamboo fiber hemostatic gauze and preparation method thereof
  • Compound pseudo-ginseng, kaolin and bamboo fiber hemostatic gauze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0043] The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.5g kaolin, 0.3g notoginseng hemostatic powder, 2g1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol Alcohol 600, 77.2g water; carry out mechanical stirring to make it fully mixed to make a suspension of 100ml. Bamboo fiber gauze is cut into 7cm * 70cm, as the base material. Using the spray-freeze drying method, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K. Finally, the prepared compound notoginseng kaolin ...

Embodiment 2

[0045] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0046] The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.6g kaolin, 0.3g notoginseng hemostatic powder, 2g1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol Alcohol 600, 77.4g water; carry out mechanical stirring to make it fully mixed to make a suspension of 100ml. Bamboo fiber gauze is cut into 7cm * 70cm, as the base material. Using the spray-freeze drying method, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K. Finally, the prepared compound notoginseng kaolin ...

Embodiment 3

[0048] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0049] The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.8g kaolin, 0.4g notoginseng hemostatic powder, 2g1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol Alcohol 600, 76.8g water; carry out mechanical stirring to make it fully mixed to make a suspension of 100ml. Bamboo fiber gauze is cut into 7cm * 70cm, as the base material. Using the spray-freeze drying method, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K. Finally, the prepared compound notoginseng kaolin ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of medical dressings and production processes of medical dressings, and in particular relates to a compound pseudo-ginseng, kaolin and bamboo fiber hemostatic gauze and a preparation method thereof. The hemostatic gauze comprises a base material, a hemostatic material and a binding agent, wherein the base material is made of a raw or regenerated bamboo fiber material; the hemostatic material is bonded to the base material; the binding agent is used for binding the hemostatic material to the base material; and the hemostatic material comprises a kaolin or kaolinite hemostatic clay material and pseudo-ginseng hemostatic powder. The base material of the hemostatic gauze provided by the invention comprises bamboo fiber, the hemostatic material comprises kaolin or kaolinite and pseudo-ginseng hemostatic powder, and the hemostatic clay material and the pseudo-ginseng hemostatic powder are bound to the bamboo fiber of the base material by using the binding agent, so that the hemostatic gauze is stable in property, the hemostatic clay material or the pseudo-ginseng hemostatic powder is not easy to drop off, and the hemostatic gauze is good in hemostatic effect.

Description

technical field [0001] The invention relates to the technical field of medical dressings and production techniques thereof, in particular to a compound notoginseng kaolin bamboo fiber hemostatic gauze and a preparation method thereof. Background technique [0002] Blood loss is the primary factor of traumatic death, and at least 30% of the wounded who died due to excessive blood loss can be saved if timely and effective hemostasis can be achieved. Blood loss is also the main cause of traumatic death such as war wounds and falling injuries. Successful hemostasis within an effective time is of great significance to saving lives. All countries in the world attach great importance to the research on post-traumatic hemostasis measures. But at present the hemostatic gauze that domestic emergency is used still stays at the level of non-woven gauze, there is still no effective, composite hemostatic gauze that can be used for first aid so far. In order to solve this problem, it is n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/40A61L15/44A61L15/58A61L15/28A61L15/26A61K36/258A61P7/04A61K33/06
CPCA61L15/40A61K33/06A61K36/258A61L15/26A61L15/28A61L15/44A61L15/58A61L2300/10A61L2300/418A61L2300/45C08L1/02C08L71/02A61K2300/00
Inventor 张宜樊光辉刁波喻晶黎檀石
Owner WUHAN GENERAL HOSPITAL OF GUANGZHOU MILITARY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com