Knitting method for warp-knitted spacer fabric with different thicknesses

A technology of warp-knitting spacer fabrics and fabrics, which is applied in warp knitting, knitting, textiles and papermaking, and can solve problems such as inability to produce free-form objects

Inactive Publication Date: 2016-12-07
JIANGNAN UNIV
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Free-form stuffed textile objects can be used in a variety of applications, from two-dimensional to three-dimensional, but all have the disadvantage that the object will tilt outward due to internal air pressure and m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Knitting method for warp-knitted spacer fabric with different thicknesses
  • Knitting method for warp-knitted spacer fabric with different thicknesses
  • Knitting method for warp-knitted spacer fabric with different thicknesses

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1: Concave-convex effect formed laterally

[0039] On the E22 double needle bed warp knitting machine, six bars are used for knitting, and the distance of the looper board is 16mm. The fabric structure, threading and warp let-off are shown in Table 1:

[0040] Table 1

[0041]

[0042] When the distance of the knock-off plate is 16mm, the spacer wire of GB3 has 2 rows of normal loops on the front and rear needle beds, and the let-off amount of the loop is 17327mm / rack, but at this time the spacer wire of GB4 is the same on the front and rear needle beds. 2 When the loop is formed in a row, the let-off amount is greater than the normal let-off amount, which is 24000mm / rack. GB3 and GB4 have 10 courses of missing pads at the same time, that is, the 10 courses, the spacer yarn is not connected to the fabric of the front and rear needle beds, but in order to achieve the thickness of the GB4 connecting yarn area greater than the thickness of the GB3 connecting yarn area, t...

Example Embodiment

[0043] Example 2: Longitudinal formation of uneven effect

[0044] On the E18 double needle bed warp knitting machine, five bars are used for knitting, and the distance of the looper board is 16mm. The fabric structure, threading and warp let-off are shown in Table 2:

[0045] Table 2

[0046]

[0047] When the distance of the knock-off plate is 30mm, the spacer wire of GB3 has 2 courses of normal loop formation on the front and rear needle beds. The let-off amount when the loop is formed is 31679mm / rack, and the let-off amount when the 8 rows are missing is 29341mm / Rack, the yarn let-off amount of the first 200 courses remains unchanged. The let-off amount of the last 200 courses is changed. The let-off amount of loops in 2 rows is 42000mm / rack, and the amount of let-off for 8 rows is 40000mm / rack. Finally, after the surface material is composited and filled on the surface of the fabric, the thickness of the rear 200 course area is greater than the first 200 course area, such as ...

Example Embodiment

[0048] Example 3: Concave-convex effects are simultaneously formed horizontally and vertically

[0049] On the E22 double needle bed warp knitting machine, six bars are used for knitting, and the distance of the looper board is 30mm. The fabric structure, threading and warp let-off are shown in Table 3:

[0050] table 3

[0051]

[0052]

[0053] When the distance of the knock-off plate is 30mm, the spacer wire of GB3 has 2 courses of normal loop formation on the front and rear needle beds, the let-off amount when the loop is formed is 17327mm / rack, and the let-off amount when the 8 rows are missing is 6000mm / Rack, the interval wire let-off amount of the first 100 courses remains unchanged. In GB4, the warp let-off amount for normal loop formation of 2 rows of GB4 becomes 24000mm / rack, the warp let-off amount when the pad is missing for 8 rows is changed to 9000mm / rack, and the warp let-off amount of the spacer wire of the first 100 rows remains unchanged. The warp let-off amount ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a knitting method for a warp-knitted spacer fabric with different thicknesses. The warp-knitted spacer fabric is knitted by adopting six guide bars on a double-needle bar warp knitting machine, and the knitting method is characterized by comprising the following steps: (1) penetrating an upper surface layer yarn into guide bars GB1 and GB2, penetrating a lower surface layer yarn into guide bars GB5 and GB6, and penetrating a spacer yarn into guide bars GB3 and GB4, wherein the upper surface layer of the fabric is knitted by the guide bars GB1 and GB2, the lower surface layer of the fabric is knitted by the guide bars GB5 and GB6, and the spacer yarn is knitted by the guide bars GB3 and GB4; (2) when the thickness is changed in the transverse direction, penetrating the yarn by the guide bars GB3 and GB4 complementarily, wherein the yarn penetrating amounts of the guide bars GB3 and GB4 are equal, the guide bar GB3 penetrates the yarn first and then is spaced, and the guide bar GB4 is spaced first and then penetrates the yarn; the warp feeding amount of the guide bar GB3 is set to be smaller than that of the guide bar GB4; (3) when the thickness is changed in the longitudinal direction, setting the set warp feeding amount of part transverse area in the longitudinal row of the guide bar GB3 or the guide bar GB4 to be great, and setting the set warp feeding amount of part transverse area in the longitudinal row of the guide bar GB3 or the guide bar GB4 to be small. According to the knitting method for the warp-knitted spacer fabric with different thicknesses, the transverse cross section and the longitudinal cross section of the fabric can have different thicknesses by controlling the yarn penetrating amount and the warp feeding amount.

Description

technical field [0001] The invention relates to a weaving method of warp-knitted spacer fabrics with different thicknesses, in particular to a weaving method of three-dimensional three-dimensional textiles with surface concave-convex effects. Background technique [0002] The double-needle-bed warp-knitted spacer fabric is a three-dimensional warp-knitted fabric composed of two independent surface fabrics and a spacer yarn in the middle for connection and support. It is a conventional type of double-needle-bed Raschel machine. The machine usually uses a latch needle, and the distance between the knockout plates can be adjusted to determine the distance between the outer two layers, ie the thickness of the three-dimensional textile. The thickness of the spacer fabric has a large selection range, generally 2-60mm; in order to achieve some special purposes, the thickness can be increased to 150mm, or even more. [0003] As people gradually have higher requirements for textiles...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04B21/08D06N3/00D06N3/12
CPCD04B21/08D06N3/0009D06N3/128D10B2331/04
Inventor 陈晴蒋高明缪旭红马丕波万爱兰殷芮
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap