Artificial quartz stone leopard print plate and preparation method thereof

An artificial and glass particle technology, applied in building structure, construction, covering/lining, etc., can solve the problems of poor transparency, monotonous and disharmonious patterns of artificial quartz stone patterns, and achieve bright and bright colors and good coordination. Effect

Inactive Publication Date: 2017-06-20
BITTO IND DONGGUAN
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above problems, the present invention provides an artificial quartz stone leopard plate and its preparation method, using unsaturated resin as the binding material, fully stirring with quartz sand, mixed color paste, additives, etc., and then baking , scraping, polishing and other processes to produce the artificial quartz stone leopard plate to solve the technical defects of the existing artificial quartz stone pattern plate that the transparency is not good and the pattern is monotonous and disharmonious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An artificial quartz stone leopard board, comprising the following components in parts by weight: 13 parts of unsaturated resin, 12 parts of epoxy resin, 24 parts of refined quartz sand, 25 parts of quartz powder, 0.7 parts of pigment powder, 25 parts of textured glass particles, 0.3 part of auxiliary agent, wherein said auxiliary agent includes curing agent and accelerator.

[0014] Wherein, the leopard pattern glass particles include the following components in parts by weight: 45 parts of cullet particle sheets, 10 parts of unsaturated resin, 9 parts of epoxy resin, 5 parts of leopard pattern solid material, 600 mesh fine 30 parts of sand powder and 1 part of auxiliary agent, wherein the auxiliary agent includes a curing agent and an accelerator.

[0015] The pigment powder includes the following components in parts by weight, 15 parts of carbon black powder, 60 parts of iron yellow pigment powder, and 25 parts of iron brown pigment powder.

[0016] The above-mentio...

Embodiment 2

[0020] An artificial quartz stone leopard board, comprising the following components in parts by weight: 12 parts of unsaturated resin, 12 parts of epoxy resin, 25 parts of refined quartz sand, 26 parts of quartz powder, 0.7 parts of pigment powder, 24 parts of textured glass particles, 0.3 part of auxiliary agent, wherein said auxiliary agent includes curing agent and accelerator.

[0021] Wherein, the leopard-print glass particles include the following components in parts by weight: 46 parts of broken glass particle sheets, 9 parts of unsaturated resin, 9 parts of epoxy resin, 6 parts of leopard-print solid material, 600 mesh precision 29 parts of sand powder and 1 part of auxiliary agent, wherein the auxiliary agent includes a curing agent and an accelerator.

[0022] The pigment powder includes the following components in parts by weight, 14 parts of carbon black powder, 61 parts of iron yellow pigment powder, and 25 parts of iron brown pigment powder.

[0023] The above-...

Embodiment 3

[0027] An artificial quartz stone leopard board, comprising the following components in parts by weight: 11 parts of unsaturated resin, 12 parts of epoxy resin, 26 parts of refined quartz sand, 25 parts of quartz powder, 0.7 part of pigment powder, 25 parts of textured glass particles, 0.3 part of auxiliary agent, wherein said auxiliary agent includes curing agent and accelerator.

[0028] Wherein, the leopard pattern glass particles include the following components in parts by weight: 47 parts of cullet particle sheets, 8 parts of unsaturated resin, 9 parts of epoxy resin, 6 parts of leopard pattern solid material, 600 mesh fine 29 parts of sand powder and 1 part of auxiliary agent, wherein the auxiliary agent includes a curing agent and an accelerator.

[0029] The pigment powder includes the following components in parts by weight: 14 parts of carbon black powder, 61.5 parts of iron yellow pigment powder, and 24.5 parts of iron brown pigment powder.

[0030] The above-ment...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to technical field of artificial quartz stone plates, in particular to an artificial quartz stone leopard print plate and a preparation method thereof. The artificial quartz stone leopard print plate comprises the following components by weight: 40-55 parts of broken glass particulate sheet, 6-12 parts of unsaturated resin, 6-12 parts of epoxy resin, 5-8 parts of a leopard print solid material, 25-32 parts of 600-mesh fine sand powder, and 0.3-1.2 parts of an assistant, wherein the assistant includes a curing agent an accelerator. The artificial quartz stone leopard print plate provided by the invention has the advantages of environmental protection, bright and transparent color, easy cleaning and flame retardance, etc.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an artificial quartz stone leopard plate and a preparation method thereof. Background technique [0002] The artificial quartz stone pattern plate in the prior art is usually directly made into an artificial quartz stone pattern plate by using an unsaturated resin as a binder, stirring with quartz sand, pigments, etc., and then baking. The quartz stone checkered plate produced in the prior art is usually not bright and transparent in color, and the color of the pattern is usually reflected in the color of the quartz sand and the pigment itself. The color of the pattern of such a quartz stone checkered plate is dull and disharmonious. Contents of the invention [0003] In order to solve the above problems, the present invention provides an artificial quartz stone leopard plate and its preparation method, using unsaturated resin as the binding material, fully stirring ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18E04F13/14C04B111/82
CPCC04B26/18C04B2111/00612C04B2111/82E04F13/147C04B24/281C04B14/06C04B14/022C04B14/308C04B14/22C04B2103/0068C04B24/121C04B24/02
Inventor 胡北清熊伟
Owner BITTO IND DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap