A kind of nail art aluminum foil and its manufacturing method

A manufacturing method and technology of aluminum foil, applied in chemical instruments and methods, manicure or pedicure tools, adhesive types, etc., can solve the problems of non-woven fabric detachment, dissolution and destruction of adhesive layer, etc., and achieve easy shaping , The effect of high fit and maintaining the integrity of the paste

Active Publication Date: 2020-10-09
ZHUOZHOU HAOYUAN FOIL IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the nail polish remover comes into contact with the nail aluminum foil, because the nail remover has a strong dissolving ability, it will cause dissolution and damage to the adhesive layer, and the non-woven fabric is easy to separate from the aluminum foil.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0022] A kind of manufacture method of nail art aluminum foil is characterized in that comprising the following steps:

[0023] A. Clean the surface of aluminum foil;

[0024] B. Brush the base paint on the bonding surface of the aluminum foil, and heat and cure;

[0025] C. Brush the adhesive layer paint on the cured base;

[0026] D. Paste the non-woven fabric on the base layer and heat and cure it;

[0027] E. The aluminum foil laminated with non-woven fabric is cut into sections and packaged to obtain the finished nail art aluminum foil.

[0028] In step A, before cleaning the aluminum foil, use a scraper to scrape the bonding surface of the aluminum foil to form scratches with a depth of 0.005-0.01 mm.

[0029] In step A, the aluminum foil is cleaned with a cleaning solution containing 2wt% HCl and 25wt% ethanol.

[0030] In step B, the primary coating includes, the following are parts by weight,

[0031] 120 parts of ethanol, 60 parts of xylene, 155 parts of ethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of nail-beautifying aluminum foil. The method comprises the following steps that firstly, the surface of the aluminum foil is cleaned; secondly, the bonding surface of the aluminum foil is coated with base layer paint, and heating and curing are carried out; thirdly, a cured base layer is coated with an adhesive layer; fourthly, non-woven cloth is attached to the base layer, and heating and curing are carried out; fifthly, the aluminum foil attached with the non-woven cloth is cut into sections and packaged, so that the finished nail-beautifying aluminum foil product is manufactured. By means of the method, the defects in the prior art can be overcome, so that the bonding effect between the non-woven cloth and the aluminum foil in the environment with a nail polish remover is improved.

Description

technical field [0001] The invention relates to the technical field of nail art aluminum foil production, in particular to a nail art aluminum foil and a manufacturing method thereof. Background technique [0002] At present, manicure is all the rage. And how to remove nail polish cleanly and conveniently has also become an important issue, so there are nail art foil products. At present, there are nail foil products, which are made of aluminum foil and non-woven fabric. When using it, apply nail remover on the non-woven fabric, and then wrap the non-woven fabric and nails on the finger. It can be completed in a few minutes Remove nails, and aluminum foil prevents nail remover water from leaking out, so finger movement is not affected during nail removal. This nail art foil product is very popular. However, after the nail polish remover comes into contact with the nail art aluminum foil, because the nail polish remover has a strong dissolving power, it will dissolve and d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A45D29/17B32B5/02B32B15/14B32B15/20C08G18/54C09D4/00C09D4/06C09D7/63C09J175/04
CPCA45D29/17B32B5/022B32B15/14B32B15/20C08G18/548C09D4/00C09D4/06C09D7/63C09J175/04
Inventor 张建
Owner ZHUOZHOU HAOYUAN FOIL IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com