Ceramic underglaze color material and manufacturing method thereof

A ceramic glaze and raw material technology, which is applied in the field of ceramic manufacturing, can solve problems such as difficulties in industrialized production, unfavorable industrialized production, and poor results of finished products, and achieve the effect of reducing the difficulty of writing and drawing, good viewing and collection value, and easy writing

Active Publication Date: 2021-06-25
邵细军
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the porcelain fired with underglaze color is bright in color, acid-resistant and wear-resistant, and can be maintained permanently, due to the inherent material properties of underglaze color, it is difficult to write on larger porcelain works, such as some art porcelain. And the painting area is large, which can easily lead to uneven material color, and it is difficult to achieve the effect of fine picture and uniform color tone in the fired ceramics, so there are very few good products.
[0004] In addition, in the production of advertising signs such as porcelain boards, in addition to the above-mentioned uneven color of the material, the traditional method of engraving and then glazing and firing is also easy to cause the lower layer of material to be damaged and the upper layer of material to be suspended. Poor, time-consuming and labor-intensive, very unfavorable for industrial production
[0005] Therefore, the present invention intends to develop a kind of underglaze color material to solve the problem of uneven material color, non-uniform color tone, time-consuming carving and industrialized production of existing underglaze color materials in the preparation of porcelain works such as art porcelain or porcelain plate signboards. Difficulties and other problems, this kind of underglaze color material can change the production method of traditional art porcelain or porcelain plate signboard, not only simplify the production process, but also enable the industrial production of such porcelain, thus filling the domestic gap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic underglaze color material and manufacturing method thereof
  • Ceramic underglaze color material and manufacturing method thereof
  • Ceramic underglaze color material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044]

[0045] (1) Take 120g of deionized water, heat it to 40°C, add methacrylic acid copolymer, shear at high speed to disperse, then slowly add Tween-80, oleic acid and isocyanate, and emulsify for 2 hours to obtain an emulsion;

[0046] (2) Take 40g of deionized water, heat it to 70°C, add hydroxypropyl methylcellulose, stir to dissolve, let cool to 40°C, add N-ethyl urethane, sodium succinate sulfonate, Stir to dissolve to obtain a mixed solution;

[0047] (3) Slowly add the emulsion to the mixed solution under high-speed shear, stir at 60°C for 2 hours, cool to room temperature, then add silicon dioxide and titanium dioxide, and stir for 30 minutes to obtain the product.

Embodiment 2

[0049]

[0050] (1) Take 90g of deionized water, heat it to 40°C, add ethyl acrylate-methyl methacrylate 1:1 copolymer, shear at high speed to disperse, then slowly add Tween-80, oleic acid and isocyanate, Emulsified for 4 hours to obtain an emulsion;

[0051] (2) Take 40g of deionized water, heat it to 70°C, add hydroxypropyl methylcellulose, stir to dissolve, let cool to 40°C, add N-ethyl urethane, sodium succinate sulfonate, Stir to dissolve to obtain a mixed solution;

[0052] (3) Slowly add the emulsion to the mixture under high-speed shear, stir at 60°C for 2 hours, cool to room temperature, then add silicon dioxide and titanium dioxide, and stir for 20 minutes to obtain the product.

Embodiment 3

[0054]

[0055] (1) Take 100g of deionized water, heat it to 40°C, add dimethylaminoethyl methacrylate-methyl methacrylate 1:2 copolymer, shear at high speed to disperse, then slowly add Tween-80, Oleic acid and isocyanate were emulsified for 3.5 hours to obtain an emulsion;

[0056] (2) Take 50g of deionized water, heat it to 70°C, add hydroxypropyl methylcellulose, stir to dissolve, let cool to 40°C, add N-ethyl urethane, sodium succinate sulfonate, Stir to dissolve to obtain a mixed solution;

[0057](3) Slowly add the emulsion to the mixed solution under high-speed shear, stir at 60°C for 2 hours, cool to room temperature, then add silicon dioxide and titanium dioxide, and stir for 30 minutes to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a ceramic underglaze color material, which is composed of the following raw materials: polyacrylic acid resin, hydroxypropyl methylcellulose, N-ethyl urethane, oleic acid, Tween-80, isocyanate and succinic acid Sodium ester sulfonate, silicon dioxide, titanium dioxide, and deionized water. The underglaze color material is easy to load on the green body, has strong adhesion, uniform material color, and can quickly form a film with good peelability, which greatly reduces Difficulty in drawing, the development and use of this kind of underglaze color material solves the problems of uneven material color, inconsistent color tone, time-consuming carving and difficulties in industrial production when preparing art porcelain or porcelain board signboards and other porcelain works. It not only makes the picture of the fired porcelain fine and uniform, and has great artistic appreciation value, but also changes the traditional production method of porcelain, greatly simplifies the production process, and realizes the industrial production of works such as art porcelain and porcelain board signboards, filling the The gap in domestic technology has been filled.

Description

technical field [0001] The invention belongs to the technical field of ceramic manufacturing, and in particular relates to a ceramic underglaze color material and a manufacturing method thereof. Background technique [0002] Ceramics are utensils made of natural clay and various natural minerals through crushing, kneading, molding and calcination. In the process of ceramic preparation, the glaze color of the surface will undergo various chemical changes due to different firing temperatures. Thereby presenting different decoration styles. Among them, Jingdezhen's blue and white porcelain is one of the famous traditional Chinese porcelains. Its blue and white contrast, pleasant and interesting, crystal clear and bright, beautiful and timeless. [0003] Although the porcelain fired with underglaze color is bright in color, acid-resistant and wear-resistant, and can be maintained permanently, due to the inherent material properties of underglaze color, it is difficult to write ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/20C04B41/89
Inventor 邵细军邵振天
Owner 邵细军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap