Method for modifying PET obtained by depolymerization of polyester waste textiles, purification and polymerization and extrusion PA6

A polyester and modified technology, applied in the field of new materials for alloy extrusion, can solve the problems of landfill or incineration, inability to directly reprocess, waste of land resources and second pollution

Inactive Publication Date: 2019-09-13
PLASTIC UNION NEW MATERIAL TECH HUBEI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As we all know, except for a very small amount of existing waste textiles that are used by people using physical methods, they can neither be reused

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for modifying PET obtained by depolymerization of polyester waste textiles, purification and polymerization and extrusion PA6
  • Method for modifying PET obtained by depolymerization of polyester waste textiles, purification and polymerization and extrusion PA6
  • Method for modifying PET obtained by depolymerization of polyester waste textiles, purification and polymerization and extrusion PA6

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A method of chemically depolymerizing and purifying polymerized PET with polyester waste textiles according to the present invention, and PA6 extruded material, modified into an alloy material method is implemented according to the following process procedures:

[0010] Depolymerize polyester waste textiles with glycerin residue heated to 260-280 degrees, filter the dregs in the solution, decolorize and purify to obtain liquid PET. Prepare PET and PA6 extrusion grade raw materials according to the following parts by weight.

[0011] PET 50 copies

[0012] PA6 45 copies

[0013] Compatibilizer 5 parts

[0014] Test results

[0015]

[0016] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.

Embodiment 2

[0018] With reference to the method of Example 1, each component and parts by weight were prepared in the following ratios to prepare PET / PA6 extrusion grade raw materials.

[0019] PET 48 servings

[0020] PA6 48 copies

[0021] Compatibilizer 4 parts

[0022] Test results

[0023]

[0024] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.

Embodiment 3

[0026] Referring to Examples 1 and 2, each component and parts by weight were prepared in the following proportions to prepare PET / PA6 extrusion grade raw materials.

[0027] PET 45 parts

[0028] PA6 50 copies

[0029] Compatibilizer 5 parts

[0030] Test results

[0031]

[0032] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for modifying PET obtained by chemical depolymerization of polyester waste textiles, purification and polymerization and an extrusion-grade PA6 material to form an alloy extrusion novel material in Central Plastic Union New Material Technology (Hubei) Co., Ltd. The method comprises the following steps: performing depolymerization on the polyester waste textiles byusing glycerin residues heated to 260-280 DEG C, performing filtration, performing decolorization, performing purification, performing polymerization to form the PET, adding auxiliary agents such as acompatibilizer, adding a certain proportion of the extrusion-grade PA6 material, performing uniform mixing, and performing extrusion granulation to obtain the PET and PA6 extrusion special alloy novel material.

Description

technical field [0001] The invention discloses a method of using polyester waste textiles to chemically depolymerize, purify, polymerize into PET, and modify it with PA6 extrusion material to form a new material for alloy extrusion. [0002] technical background [0003] As we all know, except for a very small amount of existing waste textiles that are used by people using physical methods, they can neither be reused nor directly reprocessed after recycling, and can only be landfilled or incinerated. Not only wasting land resources but also causing secondary pollution. Contents of the invention [0004] The purpose of the present invention is in order to overcome the defective of above-mentioned background technology, not only completely eliminate this backward processing mode fundamentally, solve secondary pollution thoroughly. The PET and extrusion-grade PA6 materials obtained by chemical depolymerization, purification and polymerization of polyester waste spinning are m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L77/02
CPCC08L67/02C08L77/02C08L2207/20
Inventor 邓忠权邓军邓丽
Owner PLASTIC UNION NEW MATERIAL TECH HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap