Glass ink and highly reflective backsheet glass
A technology of glass ink and glass powder, which is applied in the direction of ink, photovoltaic power generation, electrical components, etc., can solve the problem of glaze layer discoloration, etc., and achieve the effect of improving quality stability, product production yield and commercial profit
Pending Publication Date: 2020-11-17
信义光伏产业(安徽)控股有限公司
View PDF0 Cites 5 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] The purpose of this application is to provide a glass ink and a highly reflective backplane glass, aiming to solve the problem of discoloration of the glaze layer in the PID test of the existing high reflection backplane glass
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0050] This embodiment provides a glass ink, comprising the following components in weight percent:
[0051]
Embodiment 2
[0053] This embodiment provides a glass ink, comprising the following components in weight percent:
[0054]
Embodiment 3
[0056] This embodiment provides a glass ink, comprising the following components in weight percent:
[0057]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More
Abstract
The invention relates to the technical field of photovoltaic glass, and provides glass ink and high-reflection backboard glass. The glass printing ink provided by the invention is composed of powder and an oil agent, wherein the powder comprises glass powder, titanium dioxide and an inorganic reducing agent, and the weight percentage of the inorganic reducing agent in the glass printing ink is 2%-5%. The glass ink is used for forming a high-reflection glaze layer of the high-reflection back plate glass, titanium dioxide in the high-reflection glaze layer is effectively prevented from being oxidized during PID testing by adding an inorganic reducing agent with a specific content into powder; in addition, the problem that the glaze layer of the high-reflection back plate glass changes colorduring PID testing is solved by means of the rutile type titanium dioxide.
Description
technical field [0001] The application belongs to the technical field of photovoltaic glass, and in particular relates to a glass ink and a highly reflective back glass. Background technique [0002] Solar photovoltaic glass is a special glass that is laminated into solar cells, can use solar radiation to generate electricity, and has related current extraction devices and cables. It is composed of low-iron glass, solar cell, film, back glass, and special metal wires. The solar cell is sealed between a piece of low-iron glass and a piece of back glass through the film. It is the most innovative high-tech building. Glass products. [0003] At present, double-glass modules are developing rapidly with an irresistible trend. Double-sided power generation can bring more power generation to the power station, thereby reducing the cost of electricity. Double-glass modules use high-reflective backplane glass, and add silk screen grid patterns on the basis of traditional backplane ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
IPC IPC(8): C09D11/03C09D11/38H01L31/048H01L31/054
CPCC09D11/03C09D11/38H01L31/0488H01L31/0481H01L31/0547Y02E10/52
Inventor 李友情邵世强刘笑荣徐小明李晓东陈林唐法君陶恺
Owner 信义光伏产业(安徽)控股有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com