Anticorrosive epoxy acrylic paint
An epoxy acrylic, anti-corrosion coating technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of slow drying, water resistance, chemical resistance difficult to meet requirements, mechanical properties, water resistance and other problems
Inactive Publication Date: 2003-01-08
JIANGSU RONGCHANG NEW MATERIAL TECH
View PDF0 Cites 10 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] Traditional thermoplastic acrylic coatings have the characteristics of convenient construction and good drying performance, but their mechanical properties and water resistance are not ideal, so they have been used as topcoats for a long time, while primers generally use alkyd, epoxy, polyurethane and other coating systems
However, these systems dry slowly during use and cannot meet the requirements of on-site construction.
The epoxy-modified acrylic resin made by reacting epoxy resin with acrylic resin or cold splicing improves the mechanical properties of the film-forming material. However, the epoxy group and hydroxyl group on the epoxy resin do not participate in cross-linking, so that the The water resistance and chemical resistance of the coating composed of it are difficult to meet the requirements after the film is formed. In addition, when using this epoxy-modified acrylic coating as a primer, if the color of the top coat is light and the color of the primer is dark, it is easy to Bleeding
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
example 1～3
[0017] Use a balance to weigh each component according to the formula shown in Table 1 for subsequent use. Soak the pigment in a solvent for 1 hour, add base material and dispersant, pre-mix with a high-speed disperser for 10-15 minutes, then grind and disperse with a sand mill until the fineness is less than 40 μm, filter and pack.
example 1
[0023] Base material in example 1: pigment: solvent: dispersant is 20.00: 33.4: 44.30: 0.50, and wherein the ratio of cathode and anode corrosion-inhibiting pigment is 100: 15.94;
example 2
[0024] Base material in example 2: pigment: solvent: dispersant is 20.00: 30.026: 44.00: 0.50, and wherein the ratio of negative and negative corrosion-inhibiting pigments is 100: 28.94;
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| viscosity | aaaaa | aaaaa |
| water resistance | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
Login to view more
Abstract
The invention relates to epoxy crylic acid anti-corrosino paint, it is made up of base material, pigment, solvent and dispersant, the resin used as base material is epoxy acroid resin which contains silica alkyl and high strength polar radicel, acid value of the resin is 3-8, epoxy equivalent is 0.02-0.50, under 25 deg.C and 50% solid shares, the viscosity of the resin is 400-1500 mPa.s, the content of epoxy in molecular is 2-10%, the content of silica alkyl is 0.3-3.5%, the content of high strength polar radicel is 2-10%; What used as pigment is compound antirust pigment which is made up of chemical antirust pigment and physical antirust pigment, the weight proportion of each element in the paint is as follows: base material (counted by solid) 20-25, pigment 28-40, solvent 40-45, dispersant 0.4-6, it can be used as primer.
Description
technical field [0001] The invention relates to an epoxy acrylic anticorrosion coating, which is especially suitable for use as a primer. Background technique [0002] Traditional thermoplastic acrylic coatings have the characteristics of convenient construction and good drying performance, but their mechanical properties and water resistance are not ideal, so they have been used as topcoats for a long time, while primers generally use alkyd, epoxy, polyurethane and other coating systems . However, these systems dry slowly during use and cannot meet the requirements of on-site construction. The epoxy-modified acrylic resin made by reacting epoxy resin with acrylic resin or cold splicing improves the mechanical properties of the film-forming material. However, the epoxy group and hydroxyl group on the epoxy resin do not participate in cross-linking, so that the The water resistance and chemical resistance of the coating composed of it are difficult to meet the requirements ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D133/14
Inventor 常春周海清徐子清
Owner JIANGSU RONGCHANG NEW MATERIAL TECH
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap