Additive of phenolic resin, phenolic resin therewith and production thereof

A phenolic resin and additive technology, applied in the direction of adhesive additives, non-polymer adhesive additives, aldehyde/ketone condensation polymer adhesives, etc., can solve the problem of high price, underutilization of fenugreek, influence Adhesive curing performance and bonding strength and other issues, to achieve the effect of reducing manufacturing costs, reducing the amount of resin, and reducing the content of phenolic resin

Inactive Publication Date: 2007-12-05
BEIJING FORESTRY UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of general protein is high, and the curing performance and bonding strength of the adhesive are often affected when the amount added is too much, which limits its use.
At present, there is a kind of fenugreek rich in protein and polysaccharide that has not been fully utilized, and its utilization is limited to medicinal and biological glue, and its utilization rate is about 30%, and about 70% of the remaining residues are discarded and have not been effectively used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1) Prepare a sodium carbonate solution with a concentration of 5%. Add 25kg of fenugreek residue powder to 75kg of sodium carbonate solution, stir and heat to 70-80°C, react for 3-6 hours, cool to 30°C, and obtain a viscosity of 200 -400cP homogeneous fenugreek residue mucilage.

[0018] 2) Mix the obtained fenugreek residue mucus with an alkaline water-soluble phenolic resin with a molar ratio of phenol and formaldehyde of 1:2.1 in a ratio of 30:70 by weight to prepare a phenolic resin adhesive.

[0019] Among them, the performance index of fenugreek residue mucus is as follows:

[0020] Appearance: yellow-brown mucus

[0021] pH: 9-11

[0022] Solid content: 25-30%

[0023] The quality indicators of the adhesive are as follows:

[0024] Solid content 30-40%

[0025] pH 10.0-11.0

[0026] Viscosity (20℃) 150-300mPa·s

[0027] Free formaldehyde content <0.2%

[0028] Free phenol content <0.2%

[0029] Storage period 2-3 months

[0030] The phenolic resin molar...

Embodiment 2

[0044] 1) Prepare a sodium carbonate solution with a concentration of 5%, add 25kg of fenugreek residue powder to 75kg of the solution, stir and heat to 70-80°C, react for 3-6 hours, cool down to 30°C, and obtain a solution with a viscosity of 200-400cP Evenly fenugreek residue mucilage.

[0045] 2) The obtained fenugreek residue mucus and the same alkaline water-soluble phenolic resin as in Example 1 were uniformly mixed in a ratio of 50:50 by weight to make a phenolic resin adhesive.

[0046] The adhesive quality index:

[0047] Solid content 30-40%

[0048] pH 9.5-10.5

[0049] Viscosity (20℃) 150-300mPa·s

[0050] Free formaldehyde content <0.2%

[0051] Free phenol content <0.2%

[0052] Storage period 60-90 days

experiment example

[0065]Utilize the phenolic resin binder that the phenolic resin of the embodiment of the present invention 1,2 method and comparative example 1 and comparative example 2 method prepare respectively to manufacture seven-layer plywood, adopt following preparation process parameter:

[0066] Veneer: Poplar, thickness 1.6mm;

[0067] Glue adjustment: each glue type is added with flour according to 10% of the total weight, and mixed evenly;

[0068] Glue sizing: gluing on the core board, the amount of gluing is 220~300g / m 2 ;

[0069] Aging: 10-30 minutes;

[0070] Hot pressing: 130°C, 1.5MPa, 70s / mm.

[0071] The performance test results of the seven-layer plywood manufactured by the above process are shown in Table 1, and the bonding strength was measured according to the provisions of GB / T17657-1999 "Test Methods for Physical and Chemical Properties of Wood-based Panels and Decorated Wood-based Panels".

[0072] Table 1 Formaldehyde emission and bonding strength of glued ply...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

An additive of phenolic resin, phenolic resin containing it and its production are disclosed. The procedure is carried out by mixing 3-25% sodium carbonate solution 70-80 proportion with gynesin residue powder 20-30 proportion, heating to 70-80 degrees C, reacting for 3-6hrs, lowering temperature to 30 degrees C to obtain homogeneous 200-400mPas gynesin residue mucus as additive of phenolic resin, mixing alkali soluble phenolic resin with gynesin residue powder in proportion of 90-50:10-50 and obtain the final product. It is cheap and has less formaldehyde releasing account.

Description

technical field [0001] The present invention relates to an additive for an adhesive, an adhesive based on an organic polymer compound containing the additive and a preparation method thereof, in particular to an additive for a phenolic resin for wood-based panels, a phenolic resin containing the additive and its preparation method. Background technique [0002] With the rapid development of construction, decoration, packaging and other industries, the output of wood-based panels in my country has increased rapidly, and the adhesives for wood-based panels have also developed rapidly. The types of adhesives used for wood-based panels in my country are roughly the same as those in foreign countries. The commonly used "trialdehyde adhesives" include urea-formaldehyde resins, phenolic resins and melamine-formaldehyde resin adhesives, which occupy a dominant position. Among them, phenolic resin is an excellent and widely used glue type in wood adhesives, and phenolic resin is the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J161/06C09J11/02
Inventor 李建章周文瑞任强赵金平王建中陈欣赵强母军
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap