Combined mould for precasting ring-type forge piece cast steel billet

A combined mold and ring forging technology, which is applied in the field of mechanical forging and casting, can solve the problems of mold bodies stuck together and cannot be separated, cracks or cracks, scrapping, etc., to reduce production costs, simplify forging process, and simple method and structure Effect

Inactive Publication Date: 2008-02-13
齐虎成
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the selection of conventional draft angle values ​​during the discussion process, the annular inner side of the cast billet and the lower mold body of the mold are stuck together and cannot be separated, or cracks are likely to occur on the carrier surface of the cast billet or cracks to form scrap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined mould for precasting ring-type forge piece cast steel billet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The present invention will be further described below in conjunction with accompanying drawing:

[0014] In Fig. 1 and Fig. 2: annular casting billet 1, lower mold body 2, inner ring body 3, small ring block 4, small wedge block 5, annular surface 6.

[0015] In the embodiment shown in the drawings, the inner ring body 3 of combined structure is provided in the annular cavity of the lower mold body 2, and the inner ring body 3 is arranged in the concave step at the bottom of the cavity of the lower mold body 2, and the inner ring body 3 The ring body 3 is composed of two small ring blocks 4 and two small wedge blocks 5 respectively. The upper end surface, and the annular outer surface of the inner ring body 3, that is, the cavity surface in contact with the annular cast billet 1, is provided with a concave isosceles triangular annular surface 6, and the draft slope is not selected.

[0016] During use, it is enough to assemble the inner ring body 3 of the combined stru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an annular forge-piece cast ingot prefabricating combined mould for separating the cast ingot from the bottom molding body and preventing the cast ingot body from producing cracks or rips. Its technical key points: setting combined inner ring body in the die space of the bottom molding body, where the inner ring body is composed of two, three or four small ring or wedge blocks, and there is a concave-arc or concave-isoceles triangular annular surface on the inner ring body.

Description

technical field [0001] The invention relates to the technical field of mechanical forging and casting, in particular to a special mold for manufacturing a prefabricated part of a ring-shaped forging whose cross-section is circular or rectangular, that is, a cast billet. Background technique [0002] At present, ring-shaped mechanical parts with a large load and special technical requirements, with circular or rectangular cross-sections and large geometric dimensions and weights, are all made of forgings made by free forging through machining and other processes. ; Both heat the hot-rolled square steel with a side length of 200-300 mm to the forging temperature and then cut it with a chisel or chop it, then heat the billet for the second time and upsetting, punching, and then pass through the third time After heating, reaming and forming; the forging can be formed when it has a rectangular cross-section, and it can only be pre-formed when its forging is a circular cross-secti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21J5/02
Inventor 胡补元齐虎成
Owner 齐虎成
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap